Integrating micro- and nanowaste glass with waste foundry sand in ultra-high-performance concrete to enhance material performance and sustainability

Dong Zheng,Ali H. AlAteah,Ali Alsubeai,Sahar A. Mostafa

DOI: https://doi.org/10.1515/rams-2024-0012

2024-01-01

REVIEWS ON ADVANCED MATERIALS SCIENCE

Abstract:Abstract The utilization of waste glass with micro- and nanoparticles in ultra-high-performance concrete (UHPC) has garnered significant interest due to its potential to enhance sustainability and material performance. This study focuses on the implications of integrating microwaste glass (MG) and nanowaste glass in the presence of waste foundry sand and its impact on the properties of UHPC. The particular emphasis of the current work is on compressive strength, tensile strength, sorptivity, and microstructure. It is found that MG enhances compressive strength, decreased tensile strength, reduced sorptivity, and a more compact microstructure. The results indicate that replacing cement with 20% microglass achieves the optimal compressive strength by increasing up to 11.6% at 7 days, 9.5% at 28 days, and 10.18% at 56 days. Nanowaste glass, owing to its increased reactivity and larger surface area, accelerates calcium silicate hydrate formation and improves compressive strength. At the same time, the effective utilization of nanowaste glass improves long-term resilience with an optimum compressive strength at 1.5% replacement ratios of 17.5, 18.9, and 16% at 7, 28, and 56 days, respectively. Splitting tensile strength increased by 16% at 20% MG and 21% at 1.5% nanowaste glass, respectively. Utilizing MG and nanowaste glass in UHPC with waste foundry sand is a promising method for boosting material performance and minimizing environmental impact.

materials science, multidisciplinary,nanoscience & nanotechnology

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to improve the performance and sustainability of materials by integrating micron - and nano - scale waste glass powder and foundry waste sand in Ultra - High Performance Concrete (UHPC). Specifically, the focus of the research is on evaluating the impact of these materials on the compressive strength, tensile strength, water absorption rate and microstructure of UHPC.

### Main Research Questions
1. **Improving the Mechanical Properties of UHPC**: By adding micron - scale waste glass (MG) and nano - scale waste glass (NWG), study their influence on the compressive strength and tensile strength of UHPC.
2. **Improving the Durability of UHPC**: Evaluate the impact of these waste materials on the water absorption rate of UHPC, thereby improving the long - term durability of the material.
3. **Optimizing the Microstructure**: Analyze the influence of MG and NWG on the microstructure of UHPC and explore how they enhance the material properties by improving the microstructure.
4. **Sustainability**: Explore the feasibility of using waste glass and foundry waste sand as alternative materials, reduce environmental impacts and improve resource utilization efficiency.

### Research Methods
- **Raw Material Preparation**: Including cement, silica fume, sand, coarse aggregate, water - reducing agent, water, micron - scale waste glass and nano - scale waste glass.
- **Mixing Ratio**: Determine the optimal mixing ratio through multiple experiments, fix the water - binder ratio at 0.173 and the silica fume content at 15%, and keep the aggregate content unchanged.
- **Specimen Preparation**: Describe in detail the mixing process and specimen preparation steps.
- **Testing Procedures**: Conduct tests such as compressive strength, splitting tensile strength, water absorption rate and microstructure analysis.

### Key Findings
- **Compressive Strength**:
- Adding 20% micron - scale waste glass (MG) increased the compressive strength by 11.6%, 9.5% and 10.18% at 7 days, 28 days and 56 days respectively.
- Adding 1.5% nano - scale waste glass (NWG) increased the compressive strength by 17.5%, 18.9% and 16% at 7 days, 28 days and 56 days respectively.
- **Splitting Tensile Strength**:
- 20% MG and 1.5% NWG increased the splitting tensile strength by 16% and 21% respectively.
- **Water Absorption Rate**:
- Adding 20% MG significantly reduced the water absorption rate of UHPC, indicating that the durability of the material has been improved.
- **Microstructure**:
- The addition of MG and NWG made the microstructure of UHPC more compact, reduced the porosity and enhanced the overall performance of the material.

### Conclusion
This research has successfully improved the compressive strength, tensile strength and durability of the material while optimizing the microstructure by integrating micron - and nano - scale waste glass powder and foundry waste sand in UHPC. This not only improves the performance of UHPC but also promotes the recycling of resources, which has important environmental and economic significance.