Promoting high-voltage stability through local lattice distortion of halide solid electrolytes

Zhenyou Song,Tengrui Wang,Hua Yang,Wang Hay Kan,Yuwei Chen,Qian Yu,Likuo Wang,Yini Zhang,Yiming Dai,Huaican Chen,Wen Yin,Takashi Honda,Maxim Avdeev,Henghui Xu,Jiwei Ma,Yunhui Huang,Wei Luo

DOI: https://doi.org/10.1038/s41467-024-45864-1

IF: 16.6

2024-02-17

Nature Communications

Abstract:Abstract Stable solid electrolytes are essential to high-safety and high-energy-density lithium batteries, especially for applications with high-voltage cathodes. In such conditions, solid electrolytes may experience severe oxidation, decomposition, and deactivation during charging at high voltages, leading to inadequate cycling performance and even cell failure. Here, we address the high-voltage limitation of halide solid electrolytes by introducing local lattice distortion to confine the distribution of Cl − , which effectively curbs kinetics of their oxidation. The confinement is realized by substituting In with multiple elements in Li 3 InCl 6 to give a high-entropy Li 2.75 Y 0.16 Er 0.16 Yb 0.16 In 0.25 Zr 0.25 Cl 6 . Meanwhile, the lattice distortion promotes longer Li-Cl bonds, facilitating favorable activation of Li + . Our results show that this high-entropy halide electrolyte boosts the cycle stability of all-solid-state battery by 250% improvement over 500 cycles. In particular, the cell provides a higher discharge capacity of 185 mAh g −1 by increasing the charge cut-off voltage to 4.6 V at a small current rate of 0.2 C, which is more challenging to electrolytes|cathode stability. These findings deepen our understanding of high-entropy materials, advancing their use in energy-related applications.

multidisciplinary sciences

What problem does this paper attempt to address?

The paper aims to address the stability and cycling performance issues of halide solid electrolytes in lithium-ion batteries under high voltage conditions. Specifically, the study introduces local lattice distortions to restrict the distribution of chloride ions (Cl⁻), effectively suppressing their oxidation kinetics. Through this method, researchers developed a high-entropy halide electrolyte (Li₂.₇₅Y₀.₁₆Er₀.₁₆Yb₀.₁₆In₀.₂₅Zr₀.₂₅Cl₆), which not only improves the conductivity of lithium ions but also significantly enhances its oxidative stability under high voltage.

The research shows that this high-entropy halide electrolyte can improve the cycling stability of all-solid-state batteries (ASSBs) by 250% and maintain a high capacity retention rate even after 500 cycles. Particularly, when the cut-off charging voltage is increased to 4.6 V, the battery exhibits a higher discharge capacity (185 mAh g⁻¹) and excellent cycling stability. These findings deepen our understanding of high-entropy materials and advance their use in energy-related applications.