Mechanism of Mn on inhibiting Fe-caused magnesium corrosion

Lei Yang,Shouzhen He,Chao Yang,Xiaorong Zhou,Xiaopeng Lu,Yuanding Huang,Gaowu Qin,Erlin Zhang

DOI: https://doi.org/10.1016/j.jma.2020.09.015

IF: 11.813

2021-03-01

Journal of Magnesium and Alloys

Abstract:In the present study, to understand the mechanism of Mn on inhibiting Fe-caused Mg corrosion, the corrosion behaviour of commercial pure Mg and Mg-6Mn alloy in 0.6 M NaCl solution is investigated. It is found that in Mg-6Mn alloy, Fe impurity is incorporated into Mn to form Mn (Fe) phase with Fe as solid solute. The initial galvanic corrosion cannot be reduced through converting Fe-rich phase to Mn (Fe) phase, since Mn (Fe) phase also has relatively strong cathodic activity and has much larger volume fraction than Fe-rich phase. However, the cathodic activation behaviour of pure Mg is inhibited. The cathodic activity even decreases for Mg-Mn alloy with increased exposure time, due to the reduced cathodic HER at the Mn (Fe) particles. Mn can be oxidized at the OCP of Mg-6Mn alloy, resulting in relatively dense Mn-rich corrosion film on particle surface, which separates the particle from the electrolyte and, consequently, inhibits HER.

metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper mainly discusses how to prepare uniform ultra-single crystal alloys using Electric-Magnetic-Compound field assisting solidification technology. In the study, the authors used a zinc-30wt% bismuth alloy and conducted experiments at different Electric Magnetic Body Forces (EMBF) and frequencies. They found that a uniform solid structure could be achieved under a low cooling rate (25K/min) when the EMBF magnitude was 85N/cm³ and the frequency was 50Hz. This is the first time that a uniform ultra-single crystal alloy has been obtained under such conditions.

Physical simulation experiments were also conducted in the paper to reveal how EMBF mixes the layered melt and slows down the movement of droplets. Two physical models were proposed to explain how EMBF reduces the droplet velocity. The experimental results showed that both lower or higher EMBF frequencies cannot effectively break the layered structure, while moderate EMBF frequencies can achieve a more uniform alloy structure. In addition, EMBF affects droplets in two ways: breaking them into smaller pieces through the alternating direction characteristic, and changing the droplet's path, both of which reduce collisions between droplets and facilitate the formation of a uniform solid structure.

In summary, this paper aims to address the issue of obtaining a uniform structure in ultra-single crystal alloys using traditional casting methods and proposes a new preparation method, which is to utilize Electric-Magnetic-Compound field assisting solidification technology to achieve a uniform distribution of alloy composition.