Platinum–Ruthenium Dual‐Atomic Sites Dispersed in Nanoporous Ni0.85Se Enabling Ampere‐Level Current Density Hydrogen Production

Lebin Cai,Haoyun Bai,Cheng‐wei Kao,Kang Jiang,Hui Pan,Ying‐Rui Lu,Yongwen Tan

DOI: https://doi.org/10.1002/smll.202311178

IF: 13.3

2024-01-17

Small

Abstract:In this paper, Pt‐Ru dual‐atomic‐sites co‐embedded in nanoporous nickel selenides are developed through a rapid melt‐quenching approach and chemical etching method. The strong intracrystal electronic metal‐support interaction (IEMSI) between Pt‐Se‐Ru sites and Ni0.85Se support greatly enlarge the charge redistribution density, which enables the highly‐efficient hydrogen production under an industrial‐level current density. Alkaline anion‐exchange‐membrane water electrolyzers (AEMWEs) using earth‐abundant catalysts is a promising approach for the generation of green H2. However, the AEMWEs with alkaline electrolytes suffer from poor performance at high current density compared to proton exchange membrane electrolyzers. Here, atomically dispersed Pt‐Ru dual sites co‐embedded in nanoporous nickel selenides (np/Pt1Ru1‐Ni0.85Se) are developed by a rapid melt‐quenching approach to achieve highly‐efficient alkaline hydrogen evolution reaction. The np/Pt1Ru1‐Ni0.85Se catalyst shows ampere‐level current density with a low overpotential (46 mV at 10 mA cm−2 and 225 mV at 1000 mA cm−2), low Tafel slope (32.4 mV dec−1), and excellent long‐term durability, significantly outperforming the benchmark Pt/C catalyst and other advanced large‐current catalysts. The remarkable HER performance of nanoporous Pt1Ru1‐Ni0.85Se is attributed to the strong intracrystal electronic metal‐support interaction (IEMSI) between Pt‐Se‐Ru sites and Ni0.85Se support which can greatly enlarge the charge redistribution density, reduce the energy barrier of water dissociation, and optimize the potential determining step. Furthermore, the assembled alkaline AEMWE with an ultralow Pt and Ru loading realizes an industrial‐level current density of 1 A cm−2 at 1.84 volts with high durability.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology