Abstract:Ternary metal layered double hydroxide compounds are used as electrode materials to increase the specific capacitance of supercapacitors. Improvement of the substrate material also benefits the electrode material, which already displays excellent electrochemical properties. In this study, nickel foam (NF) was cleaned and then modified by chemical plating, which can significantly improve the corrosion resistance and retain the optimal electrical conductivity properties of the metallic material. This is because of the typically amorphous structure of the chemically plated NiP alloy. It also makes NF less susceptible to corrosion under strong alkaline conditions. Co-ZIF-67 was then prepared by a facile method, and NiMo-LDH was grown by controlling the duration of hydrothermal reaction during NF/ treatment. Finally, NF/ composites with embroidered spherical nanosheets of NiMoCo-LDH (NMC-LDH) were synthesized on NF/Ni-P and used to encourage the non-binder direct growth of electrodes. The binder-free electrode, NF/, exhibited outstanding electrochemical properties in 6 mol of KOH, including an ultra-high specific capacitance of 2980 F g −1 at 1 A g −1 and a capacitance retention of 82.95 % at 10 A g −1 . The cycle performance was also much higher compared to , with good cycle stability (82.68 % at 10 A g −1 after 5000 cycles). The NF///AC ASC showed a high specific energy at 727.9 W·kg −1 , generating 91.2 Wh·kg −1 with excellent capacity retention (86.97 % after 5000 cycles). Therefore, this work can provide new ideas for improving the specific capacitance of supercapacitors and preparing new electrode materials, which may have multiple application potentials in the whole energy storage industry.

Novel fabrication strategy of nanostructured NiCo-LDHs monolithic supercapacitor electrodes via inducing electrochemical in situ growth on etched nickel foams

A Metal-Organic Framework Derived Hierarchical Nickel-Cobalt Sulfide Nanosheet Array on Ni Foam with Enhanced Electrochemical Performance for Supercapacitors

Rapid Synthesis of Mn-Doped NiFe2O4 Nanosheet Arrays for High-Performance Hybrid Supercapacitors

High-Performance Ni-Co Sulfide Nanosheet-Nanotubes Grown on Ni Foam As a Binder Free Electrode for Supercapacitors

Synthesis of NiMn-LDH Nanosheet@Ni 3 S 2 Nanorod Hybrid Structures for Supercapacitor Electrode Materials with Ultrahigh Specific Capacitance

Hierarchical Structure Electrodes of NiO Ultrathin Nanosheets Anchored to NiCo2O4 on Carbon Cloth with Excellent Cycle Stability for Asymmetric Supercapacitors

In Situ Growth of Nico2s4 Nanotube Arrays on Ni Foam for Supercapacitors: Maximizing Utilization Efficiency at High Mass Loading to Achieve Ultrahigh Areal Pseudocapacitance

In situ electrochemical rapid growth NiCo-LDH as a high-performance electrode material for all-solid-state flexible hybrid supercapacitors

Nickel–Cobalt Layered Double Hydroxide Nanosheets for High‐performance Supercapacitor Electrode Materials

Dual role of nickel foam in NiCoAl-LDH ensuring high-performance for asymmetric supercapacitors

Ternary NiMoCo-layered double hydroxides grown on chemically plated Ni P alloyed nickel foam for high-performance supercapacitors

In situ growth of NiCo2O4 nanosheets arrays on Ni foam for high-performance supercapacitor

In‐Situ Colloidal Synthetic Route to Monodispersed NiCo2S4 Nanoparticles over Nickel Foam for High‐Performance Supercapacitive Charge Storage

Simple electrodeposition of 3D NiCoFe-layered double hydroxide nanosheet assembled nanospheres/nanoflowers on carbon cloth for high performance hybrid supercapacitors

Fabrication of hierarchical NiCo2S4 nanotubes@NiMn-LDH nanosheets core-shell hybrid arrays on Ni foam for high-performance asymmetric supercapacitors

Nickel-cobalt layered double hydroxide fabricated on TiO2/C nanofiber arrays as free standing electrode for high performance supercapacitors

A Fast and Mild In-Situ Oxidization Method to Fabricate the Nickel–cobalt Layered Double Hydroxides on Ni Foam As the High-Performance Electrode Materials

NiCo layered double hydroxide nanocages for high-performance asymmetric supercapacitors

Unique hollow fries-like NiCo-LDH material derived from NiCo-MOF with significant advantages of high-performance supercapacitors

Rational Construction of Nickel Cobalt Sulfide Nanoflakes on CoO Nanosheets with the Help of Carbon Layer As the Battery-Like Electrode for Supercapacitors

2-nm-Thick NiCo LDH@NiSe Single-Crystal Nanorods Grown on Ni Foam as Integrated Electrode with Enhanced Areal Capacity for Supercapacitors