Synthesis of 2D layered Nb2SnC at low sintering temperature and its application for high-performance supercapacitors

Zhiguo Zhang,Xiao Huang,Wenxin Lu,Xinping Qiu,Tingli Ma,Wu Xia

DOI: https://doi.org/10.1016/j.jssc.2020.121425

IF: 3.3

2020-08-01

Journal of Solid State Chemistry

Abstract:<p>Two-dimensional (2D) material of Nb₂SnC was prepared by a mild and simple solid-state reaction for high performance supercapacitors. The prepared Nb₂SnC were etched and further exfoliated in diverse solvents. The morphology development was observed by SEM and the results suggest Nb₂SnC treated by hydrofluoric solution (HF) and dimethyl sulfoxide (DMSO) in sequence has a large surface area. Moreover, the phase and chemical properties of treated Nb₂SnC were characterized by XRD, EDS and XPS. In this work, the electrochemical performances were recorded by Solartron 1287 Potentiostat Galvanostat workstation. It is revealed that the specific capacitance (Cs) of pristine Nb₂SnC is only 25 ​F ​g⁻¹ at a scanning rate of 2 ​mV ​s⁻¹. Remarkably, the Cs was increased to 128 ​F ​g⁻¹ at the same scanning rate after etched by HF for 48 ​h. Upon optimization, Nb₂SnC–HF exfoliated by DMSO exhibits a capacitance of 140 ​F ​g⁻¹ owing to the large electrochemical active surface. Promoting for practical applications, Nb₂SnC based devices were assemble. The fabricated devices contributed to an energy density of 14.4 ​Wh kg⁻¹ at the power density of 36 ​W ​kg⁻¹ with a good stability within 0 V^–0.8 ​V. Therefore, Nb₂SnC is a highly promising candidate for energy storage systems with excellent electrochemical performances.</p>

chemistry, physical, inorganic & nuclear