Abstract:ZnO thin films are synthesized by an ultrasonic spray pyrolysis method, with the deposition temperature in a range between 250–450 °C. The obtained thin films are analyzed by X‐ray diffraction (XRD), atomic force microscopy (AFM), and photoluminescence (PL). The samples are used in a photocatalytic experiment to compare the degradation efficiency by methylene blue decomposition under UV irradiation. XRD patterns confirm a polycristalline wurtzite structure with preferred orientation along the (002) plane. AFM images reveal an important change in the shape and size of the grains constituting the surface. The roughness values are in the range of 17–93 nm. Thickness values of thin films deposited at 250, 350, and 450 °C are ≈0.9, 2.3, and 1.4 µ, respectively. From PL characterization, the spectra are found to be sensitive to the deposition temperature, where emission peaks with different forms and intensities are observed. One peak at 389 nm is attributed to the recombination of free excitons, and other peaks between 403–522 nm correspond to violet, blue, and green emissions indicating the presence of Zn vacancies, Zn interstitials, and oxygen vacancies, respectively, in the ZnO structure. The photocatlytic results show that the best photocatalytic efficiency of 88% is achieved by ZnO thin film deposited at 450 °C. ZnO thin films are elaborated by ultrasonic spray pyrolysis. The deposition temperature is ranging between 250 and 450 °C. X‐ray diffraction shows a wurtzite structure. Atomic force microscopy reveals that ZnO surface deposited at 450 °C is the roughest. The photoluminescence spectra indicate the presence of different types of defects. The best photocatalytic yield is obtained by ZnO deposited at 450 °C.

Effect of different Zinc precursors in Structural and Optical properties of ZnO thin films

The growth of nanoscale ZnO films by pulsed-spray evaporation chemical vapor deposition and their structural, electric and optical properties

Effect of solution concentration on surface morphology, optical properties and solar light response of ZnO thin films

Effect of Solution Concentrations on Crystal Structure, Surface Topographies and Photoluminescence Properties of ZnO Thin Films

Effect of Nucleation and Growth Kinetics on the Electrical and Optical Properties of Undoped ZnO Films

Characteristics of ZnO Films Prepared by Ultrasonic Spray Pyrolysis Method

Ethyl Zinc β-Ketoiminates and β-Amidoenoates: Influence of Precursor Design on the Properties of Highly Conductive Zinc Oxide Thin Films from Aerosol-Assisted Chemical Vapour Deposition

Effect of thickness on properties of La-doped Zinc Blende/Wurtzite ZnO thin films prepared by spray pyrolysis

Synthesis of ZnO by thermal decomposition of different precursors: photocatalytic performance under UV and visible light illumination

Synthesis, characterization and LDA+U calculations of zinc oxide nanoparticles

Preparation and optical characteristics of ZnO films by chelating sol-gel method

Preparation and Properties of Zinc Oxide Films by Spin-Coating Water Solution Precursor

Effect of Boron-doping and annealing on the structure, morphological and optical properties of ZnO films prepared by spray pyrolysis method

Structural, optical and electrical properties of ZnO thin films prepared by reactive deposition

Effect of Deposition Temperature on Morphological, Optical, and Photocatalytic Properties of ZnO Thin Films Synthesized by Ultrasonic Spray Pyrolysis Method

Effect of ZnCl2 assisted chemical bath deposition on preferred orientations and optical properties of ZnO films

Structural and Optical Properties of Electrodeposited ZnO Thin Films

Effect of precursor concentration on stoichiometry and optical properties of spray pyrolyzed nanostructured NiO thin films

Structural and morphological changes with substrate heating in zinc films synthesized by thermal vapor deposition technique

Structural and Optical Properties of ZnO Thin Films Prepared by Sol–gel Method with Different Thickness

STUDY THE OPTICAL PROPERTIES OF THE VARIOUS DEPOSITION SOLUTIONS OF ZnO NANORODS GROWN ON GLASS SUBSTRATE USING CHEMICAL BATH DEPOSITION TECHNIQUE