Abstract:The effects of rare earth erbium (Er) micro-additions on the microstructures and mechanical properties of 2024 aluminum alloy were investigated. The microstructures and fracture surfaces of specimens prepared via high-energy ball milling, cold isostatic pressing and microwave sintering were carried out by optical microscopy (OM) and scanning electron microscopy (SEM). Under the conditions of sintering heating rate of 20 min/°C and soaking time of 30 min at 490 °C, it was found that with the increase in Er addition, the grain size first decreased then increased, and it reached a minimum size of about 5 μm when the Er content was 0.6%, showing that the grains were refined. At the same time, the compactness and microhardness reached maximum levels, which were 97.6% and 94.5 HV, respectively. Moreover, the tensile strength and elongation reached the peak at 160.5 MPa and 4.4%, respectively. The dynamic mechanical response of Er/2024Al alloy with different Er content was studied through a split Hopkinson pressure bar (SHPB) at strain rates of 600 s−1 and 800 s−1, respectively. Both at the strain rates of 600 s−1 and 800 s−1, the dynamic yield stress of the specimens increased gradually with an increase in Er content. For the 0.6 wt.% Er specimen, the dynamic yield stress reached 371.3 MPa at a strain rate of 800 s−1, which was 28.2% higher than that at a strain rate of 600 s−1. When the strain rate is 800 s−1, the deformation degree of the 0.6 wt.%Er specimen is 55.3%, which is 14.7% higher than for the Er-free one, and there are adiabatic shear bands formed in the 0.6 wt.%Er specimen. Through a fracture analysis of the samples, a certain number of dimples appeared in the fracture of an impact specimen, indicating that the addition of Er improved the toughness of the material. This research can provide a reference for the development and application of high-performance aluminum alloy in automotive structural materials.

Mechanism of Er inhibiting agglomeration of in situ ZrB2 particles in aluminum matrix composites

Effects of Zr Addition on the Deformation Behavior, Microstructure and Mechanical Properties of Dental Ti Alloys

Study on Phases Formation and Modification Ability of Rare Earth Elements La, Ce, Sm and Er in Al–Zn–Mg–Cu–Zr Alloy

Effects of Zr element on the microstructure and mechanical properties of B4C/Al composites fabricated by melt stirring method

Effects of in-situ ZrB 2 nanoparticles and scandium on microstructure and mechanical property of 7N01 aluminum alloy

Microstructure and mechanical properties of Al-Mg-Mn-Er-Zr alloys fabricated by laser powder bed fusion

Effect of Minor Er Additions on the Microstructures and Mechanical Properties of Cast Al-Cu-Mg-Ag Alloys

Effect of Erbium Micro-Additions on Microstructures and Properties of 2024 Aluminum Alloy Prepared by Microwave Sintering

Microstructure and mechanical properties of TiZrVMnCu high entropy alloy by addition of Er element

The effect of zirconium on the microstructure and mechanical properties of a super-high-strength Al-Zn-Mg-Cu alloy

Effects of addition of Er and Zr on microstructure and mechanical properties of Al–Cu–Mn–Si–Mg alloy

Wear Property Of(zrb_2+al_3zr)_p/2124 Composites Synthesized by Sonochemistry Melt Reaction

Effects of rare earth Er additions on microstructure development and mechanical properties of die-cast ADC12 aluminum alloy

Effect of Er on the Hot Deformation Behavior of the Crossover Al3Zn3Mg3Cu0.2Zr Alloy

Effect of Er and Zr additions and aging treatment on grain refinement of aluminum alloy fabricated by laser powder bed fusion

Effects of Zr+Er and Zr+Y on Microstructure and Tensile Properties of Al-Mg-Si-Cu-Mn-Cr Alloys

Microstructure evolution and mechanical properties of in-situ ZrB2/Al7085 nanocomposites during hot rolling deformation

The influence of Zn addition on the microstructure and mechanical and corrosion properties of warm rolled Al mg alloys containing Er and Zr

PREPARATION AND INTERFACE ANALYSIS OF ZrB2/Al2O3 COMPOSITE POWDERS

Characteristics of microstructural and mechanical evolution in 6111Al alloy containing Al3(Er,Zr) nanoprecipitates

Effect of Zr Microalloying on the Microstructures and Strengthening Mechanism of As-Cast Al-Fe-Zr Alloys