Hydrothermal assisted synthesis of hierarchical SnO 2 micro flowers with CdO nanoparticles based membrane for energy storage applications

Ehsan Ullah,Muhammad Zia Ullah Shah,Syed Awais Ahmad,Muhammad Sajjad,Shaukat Khan,Bhargav Akkinepally,Shenghui Guo,Fatimah M. Alzahrani,Adel E.M. Yahya,Sayed M. Eldin,A. Shah

DOI: https://doi.org/10.1016/j.chemosphere.2023.138004

IF: 8.8

2023-02-03

Chemosphere

Abstract:Hierarchical nanostructures with appropriate morphology and surface functionalities are highly desired to achieve an optimized electrochemical property for active electrode materials. This work renders the facile hydrothermal synthesis of CdO, SnO 2 , and CdO–SnO 2 nanocomposite, and their capacitive performance was tested. The formation of the pure samples and their composite was committed by low-temperature Raman spectroscopy and x-ray diffraction studies which revealed the tetragonal and cubic structures of CdO and SnO 2 powder samples with good crystallinity and purity. The morphological postmortem reveals the formation of nanoparticles morphology of CdO with a highly smooth surface appearance. Besides, the SnO 2 illustrates the morphology of the micro flowers composed of ultrathin nanosheets. More specifically, the electrochemical properties indicate the pseudocapacitive charge storage mechanism based on cyclic voltammetry and chronopotentiometry analysis. The CdO–SnO 2 composite electrode displayed a higher capacitance due to additional pores/space offered for active sites and continuously allowed electrolyte ions to interact with the inner/outer surface of the electrode. These exciting findings led us to design and fabricate battery hybrid supercapacitors (BHSC) from CdO–SnO 2, and activated carbon (AC), referred to as CdO–SnO 2 //AC BHSC, attains a high power delivery (5717 W/kg), and a maximum energy density of 42 Wh/kg at low discharge rate. Noteworthy, a stable cycling performance was obtained with only 91.3% retention after 8000 cycling at a large discharge current of 10 A/g, denoting the magnificent durability of the active electrode material.

environmental sciences