Abstract:We present a systematic study of the properties of TiN films by varying the deposition conditions in an ultra-high-vacuum reactive magnetron sputtering chamber. By increasing the deposition pressure from 2 to 9 mTorr while keeping a nearly stoichiometric composition of Ti(1-x)N(x) (x=0.5), the film resistivity increases, the dominant crystal orientation changes from (100) to (111), grain boundaries become clearer, and the strong compressive strain changes to weak tensile strain. The TiN films absorb a high concentration of contaminants including hydrogen, carbon, and oxygen when they are exposed to air after deposition. With the target-substrate distance set to 88 mm the contaminant levels increase from ~0.1% to ~10% as the pressure is increased from 2 to 9 mTorr. The contaminant concentrations also correlate with in-plane distance from the center of the substrate and increase by roughly two orders of magnitude as the target-substrate distance is increased from 88 mm to 266 mm. These contaminants are found to strongly influence the properties of TiN films. For instance, the resistivity of stoichiometric films increases by around a factor of 5 as the oxygen content increases from 0.1% to 11%. These results suggest that the sputtered TiN particle energy is critical in determining the TiN film properties, and that it is important to control this energy to obtain high-quality TiN films. Superconducting coplanar waveguide resonators made from a series of nearly stoichiometric films grown at pressures from 2 mTorr to 7 mTorr show an increase in intrinsic quality factor from ~10^4 to ~10^6 as the magnitude of the compressive strain decreases from nearly 3800 MPa to approximately 150 MPa and the oxygen content increases from 0.1% to 8%. The films with a higher oxygen content exhibit lower loss, but the nonuniformity of the oxygen incorporation hinders the use of sputtered TiN in larger circuits.

Stable Oxygen Incorporation in Superconducting TaN: An Experimental and Theoretical Assessment

Experimental and theoretical assessment of native oxide in the superconducting TaN

Metastable Ta2N3 with Highly Tunable Electrical Conductivity Via Oxygen Incorporation

Growth Mechanisms of TaN Thin Films Produced by DC Magnetron Sputtering on 304 Steel Substrates and Their Influence on the Corrosion Resistance

Bulk Superconductivity in Transition Metal Oxide TaO

Fabrication of superconducting tantalum nitride thin films using infra-red pulsed laser deposition

Effect of gas Pressure on the Mechanical Properties of Sputtered TaN Films

An atomically thin oxide layer on the elemental superconductor Ta(001) surface

Effects of nitrogen composition on the resistivity of reactively sputtered TaN thin films

Stability of Ni in Nitinol Oxide Surfaces

The Stabilization of the Rocksalt Structured Tantalum Nitride

Characterization and In-situ Monitoring of Sub-stoichiometric Adjustable Tc Titanium Nitride Growth

COMPOSITION CONTROL AND ITS ELECTRICAL PROPERTIES OF TaNx THIN FILMS

Sputtered TiN films for superconducting coplanar waveguide resonators

Synthesis and characterization of nanocrystalline TaN

Oxidation behavior and atomic structural transition of size-selected coalescence-resistant tantalum nanoclusters

Role of nitrogen and tantalum in the high-temperature oxidation behavior of AlCoCr 0.5 NiTa x Ti(N) alloys synthesized by laser in situ synthesis

Structural and electrical properties of tantalum nitride thin films fabricated by using reactive radio-frequency magnetron sputtering

Oxidation Kinetics of Superconducting Niobium and a-Tantalum in Atmosphere at Short and Intermediate Time Scales

Microstructure and Mechanical Properties of TaN Thin Films Prepared by Reactive Magnetron Sputtering

Tantalum Nitride Thin Film with a Nearly Zero Temperature Coefficient of Resistance Synthesized by Magnetron Co-Sputtering