Facile one-pot hydrothermal method to prepare Sn(II) and N co-doped TiO2 photocatalyst for water splitting under visible light irradiation

Xiao-Huan Jiang,Ying-Nan Duan,Yu Tian,Meng Chen,Mao-Kun Li,Huan-Huan Liu,Wan-Liang Yang,Meng-Kui Tian

DOI: https://doi.org/10.1007/s12598-021-01810-4

IF: 6.318

2021-08-28

Rare Metals

Abstract:In this paper, a visible light-responsive Sn2+ and N co-doped TiO2 photocatalyst was prepared by facile one-pot hydrothermal method. All as-prepared samples were characterized in detail by a series of characterization approaches. The results showed that the Sn2+ and N elements were co-doped into TiO2, while the catalyst still maintains anatase crystal structure and gets irregular little nanocluster in diameter of 9–10 nm with higher specific surface area. The absorption edge of Sn2+ and N co-doped TiO2 extends to the visible light region. Compared with Sn2+-doped TiO2 and N-TiO2, the absorption edges have obvious red-shift of about 50 and 70 nm, respectively. The synergistic effect of O 2p-N 2p and O 2p-Sn 5s hybridization to form impurity levels is the main reason for the red-shift. The hydrogen production performance of the Sn2+ and N co-doping TiO2 (n(N)/n(Ti) = 1) catalyst reached the maximum value of 0.37 mmol·h−1·g−1 under visible light, which is higher than that of N-doped TiO2 and Sn2+-doped TiO2 singly. This result is due to the wider visible light region-responsive ability of Sn2+ and N co-doped into TiO2. Furthermore, mild hydrothermal methods will not make the Sn2+ oxidized to Sn4+, which make the catalysts still maintain high photocatalytic performance. This work provides a simple and mild method for the preparation of dual-element co-doped TiO2 with high crystallinity, excellent performance and broad application prospects.Graphic abstract

materials science, multidisciplinary,metallurgy & metallurgical engineering