Parameter control in synthesis of Vermiculite-CaCl 2 composite materials for thermochemical adsorption heat storage

Yong Zhang,Ziwei Chen,Yanan Zhang,Yuehong Su,Saffa Riffat

DOI: https://doi.org/10.1016/j.energy.2024.130478

IF: 9

2024-01-31

Energy

Abstract:This study utilised vermiculite as a matrix to explore various impregnation methods for synthesising vermiculite-CaCl 2 composite materials (VCMs), focusing on the impact of these methods on the performance of VCMs as thermochemical materials. Results indicate that alternative impregnation methods (e.g., multi-step, vacuum, high pressure, and high temperature) reduce VCM porosity compared to single impregnation, resulting in higher salt content as confirmed by CaCl 2 content tests. Multi-step impregnation yields VCMs with an exceptional salt content of 81.37 wt%, surpassing the highest literature value (68 wt%) and the control group VCM-s (51 wt%). Vacuum impregnation notably increases salt penetration, leading to VCM-vac having the lowest porosity. However, this reduced porosity results in lower hydration and dehydration rates. Notably, VCM-vac exhibits the highest energy storage density of 2.05 GJ/m3, which is approximately three times the reported literature values and 1.5 times greater than the study's control group VCM-s. It also exceeds the CaCl 2 -rich VCM-m by 0.2 GJ/m3. It also demonstrates superior cyclic stability, with most CaCl 2 remaining internalised, minimising agglomeration and CaCl 2 loss. The energy consumption for vacuum impregnation is estimated at 3.51 kWh/kg (salt) , indicating relatively low energy usage. The findings indicate vacuum impregnation emerges as a preferred method for synthesising thermochemical composite materials.

energy & fuels,thermodynamics