Abstract:The thermal stability of hydrothermally treated wood fibers (HWFs) is improved by removing hemicellulose in the wood fibers. HWFs and polyamide can be directly compounded to prepare hydrothermally treated wood fiber/polyamide composites (HWPACs) without any chemical additives throughout the process. The prepared composites exhibit lightweight, high‐strength, thermal stability and processability. Hybrid wood fiber/plastic composites offer a high‐value‐added utilization for agroforestry waste, which also providing a promising solution for reducing white pollution. However, the interface incompatibility between natural wood fibers and polymers significantly impairs the mechanical properties of the composites. Herein, a straightforward procedure is proposed to solve this problem, involving the removal of low‐thermal‐stability hemicellulose from wood fibers by hydrothermal pretreatment, followed by compositing with polyamide to produce hydrothermally treated wood fiber/polyamide composites (HWPACs). No chemical additives are required to improve the interface compatibility of composites, which simplifies the manufacturing process and provides environmental benefits. The effective removal of hemicellulose (78.35%) significantly increases the onset thermal degradation temperature of hydrothermally treated wood fibers (HWFs) by 27.49 °C. This prevents the generation of micro gaps during thermal processing, thereby improving the interfacial bonding strength between HWFs and polyamide. HWPACs exhibit higher mechanical strength (flexural strength 139.45 MPa) and thermal stability while maintaining a low density (1.22 g cm−3). Various lightweight, high‐strength, and multi‐shape materials can be prepared by hot pressing, injecting, and printing HWPACs, suggesting their suitability for applications in engineering structural components.

Flexible, shape-editable wood-based functional materials with acetal linkages

Flexible transparent wood with reversible photoresponsive property

Reversible Photo-, Thermal-, and Ph-Responsive Functionalized Wood with Fluorescence Emission.

Ultra-flexible flame-retardant wood composites with resistance to extreme temperatures and mildew

Functionalization of cellulose with amine group and cross-linked with branched epoxy to construct high-performance wood adhesive

Epoxy-Acrylic Polymer In-Situ Filling Cell Lumen and Bonding Cell Wall for Wood Reinforcement and Stabilization

Superflexible Wood

Superflexible Artificial Soft Wood

Programmable and flexible wood-based origami electronics

Laminated Transparent Woods with Adjustable Optical and Enhanced Mechanical Properties

Programming material compliance and actuation: hybrid additive fabrication of biocomposite structures for large-scale self-shaping

Mechanically strong, hydrostable, and biodegradable all-biobased transparent wood films with UV-blocking performance

In Situ Construction of Thermotropic Shape Memory Polymer in Wood for Enhancing Its Dimensional Stability

Wood‐Derived Functional Polymeric Materials

High‐Strength, Thermally Stable, and Processable Wood Fiber/Polyamide Composites for Engineering Structural Components

Towards high performance wood composites through interface customization with cellulose-based adhesive

Synthesis of biomass hyperbranched polyamide resin from cellulose and citric acid for wood adhesive

Fabrication of an Ultrastrong Formaldehyde-Free Wood Adhesive with an Organic-Inorganic Cross-Linking Network

Highly Mechanical Strength, Flexible and Stretchable Wood-Based Elastomers Without Chemical Cross-Linking

Towards Low Polymer Content Transparent Composites Via Novel Integration Engineering

Transparent, UV Blocking, and Strong Wood-Based Biocomposites with Isotropic Optical and Mechanical Properties