Efficient Dual-Band White-Light Emission with High Color Rendering from Zero-Dimensional Organic Copper Iodide
Linyuan Lian,Peng Zhang,Guijie Liang,Song Wang,Xi Wang,Ya Wang,Xiuwen Zhang,Jianbo Gao,Daoli Zhang,Liang Gao,Haisheng Song,Rong Chen,Xinzheng Lan,Wenxi Liang,Guangda Niu,Jiang Tang,Jianbing Zhang
DOI: https://doi.org/10.1021/acsami.1c03881
2021-05-04
Abstract:Broad-band white-light emissions from organic–inorganic lead halide hybrids have attracted considerable attention in energy-saving solid-state lighting (SSL) applications. However, the toxicity of lead in these hybrids hinders their commercial prospects, and the low photoluminescence quantum yields (PLQYs) cannot meet the requirements for efficient lighting. Here, we report a highly efficient dual-band white-light emission from organic copper iodide, (C<sub>16</sub>H<sub>36</sub>N)CuI<sub>2</sub>, which exhibits a high PLQY of 54.3% and excellent air stability. The single-crystalline (C<sub>16</sub>H<sub>36</sub>N)CuI<sub>2</sub> possesses a unique zero-dimensional (0D) structure, in which the isolated [Cu<sub>2</sub>I<sub>4</sub>]<sup>2–</sup> dimers are periodically embedded in the wide band gap organic framework of C<sub>16</sub>H<sub>36</sub>N<sup>+</sup>. This perfect 0D structure can cause significant quantum confinement and strong electron–phonon coupling, which contributes to efficient emissions from self-trapped excitons (STEs). Photophysical studies revealed the presence of two self-trapped emitting states in [Cu<sub>2</sub>I<sub>4</sub>]<sup>2–</sup> dimers, whose populations are highly sensitive to the temperature that governs the molecular environment for [Cu<sub>2</sub>I<sub>4</sub>]<sup>2–</sup> dimers and the thermal activation energy of STEs. An ultraviolet (UV) excited white light-emitting diode fabricated using this single-phase white-light emitter exhibits a high color rendering index (CRI) of 78. The new material provides a promising emitter, having a high PLQY and a high CRI simultaneously, for SSL and display applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c03881?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c03881</a>.Crystallographic data of (C<sub>16</sub>H<sub>36</sub>N)CuI<sub>2</sub> (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c03881/suppl_file/am1c03881_si_001.cif">CIF</a>)Crystal structure, SEM image, XPS spectra, PL spectra, TGA curves, and PLQY stability of (C<sub>16</sub>H<sub>36</sub>N)CuI<sub>2</sub>; CIE chromaticity coordinates of PL spectra of the (C<sub>16</sub>H<sub>36</sub>N)CuI<sub>2</sub> SCs from 97 to 337 K; PL spectra of (C<sub>16</sub>H<sub>36</sub>N)CuI<sub>2</sub> SCs fitted by the Gaussian spectra at different temperatures; and normalized PIA onsets probed at different wavelengths and TA kinetics of (C<sub>16</sub>H<sub>36</sub>N)CuI<sub>2</sub> (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c03881/suppl_file/am1c03881_si_002.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology