Effect of Gd3+ doping on microstructure and magnetic properties of Ni–Zn–Co ferrite
Zhengyu Zhang,Yujie Yang,Hao Li,Zhihao Geng,Hongyu Ding
DOI: https://doi.org/10.1007/s10854-024-13570-9
2024-09-27
Journal of Materials Science Materials in Electronics
Abstract:In this study, the Gd 3+ -doped Ni–Zn–Co ferrite was prepared by the solid-phase method. The chemical formula is called Ni 0.10 Zn 0.30 Co 0.60 Fe 2-x Gd x O 4 . The doping amount x ranges from 0 to 0.1, and the doping amount change of each sample is 0.02. The (XRD) and FTIR results showed that the sample is a cubic spinel structure. The size of the lattice parameters ranged from (8.3790 ~ 8.4037)Å. It can be observed by the SEM the morphology of the sample is hexahedral structure, the EDS results showed that the prepared samples contained Ni, Zn, Co, Fe, Gd, and O elements. Besides this, the approximate equimolar ratios of the different elements are determined, which is consistent with the nominal composition of the proposed chemical formula of the compound. The M-H loop shows the soft magnetic properties of the sample, the ( M s ) is between (77.56 ~ 92.78)emu/g and ( H c ) is between (49.20 ~ 57.38)Oe, ( M r ) is between (5.16 ~ 7.38) emu/g, and the trend of ( M s ) and ( H c ) values is approximate, indicating that the magnetism of the Ni–Zn–Co ferrite can be fine-tuned by tailoring their composition.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied