Abstract:Magnetic nanoparticles (MNPs) modified simultaneously with amorphous Fe and Mn oxides (Mag-Fe-Mn) were synthesized to remove arsenite [As(III)] from water. Mag-Fe-Mn particles were fabricated through heterogeneous nucleation technique by employing the maghemite as the magnetic core and Fe Mn binary oxide (FMBO) as the coating materials. Powder X-ray diffraction, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, and transmission electron microscopy were utilized to characterize the hybrid material. With a saturation magnetization of 23.2 emu/g, Mag-Fe-Mn particles with size of 20 -50 nm could be easily separated from solutions with a simple magnetic process in short time (within 5 min). At pH 7.0, 200 mu g/L of As(III) could be easily decreased to below 10 mu g/L by Mag-Fe-Mn particles (0.1 g/L) within 20 min. As(III) could be effectively removed by Mag-Fe-Mn particles at initial pH range from 4 to 8 and the residual As was completely oxidized to less toxic arsenate [As(V)]. The co-occurring redox reactions between Mn oxide and As(III) was confirmed by XPS analysis. Chloride, sulfate, bicarbonate, and nitrate at common concentration range had negligible influence on As(III) removal, whereas, silicate and phosphate reduced the As(III) removal by competing with arsenic species for adsorption sites. As(M) removal was not obviously affected by natural organic matter (up to 8 mg/L as TOC). Mag-Fe-Mn could be regenerated with ternary solution of NaOH, NaCl, and NaClO. Throughout five consecutive cycles, the adsorption and desorption efficiencies maintained above 98% and 87%, respectively. Mag-Fe-Mn had a larger adsorption capacity for As(III) (47.76 mg/g) and could remove trace As(III) more thoroughly than MNPs modified solely with either Fe or Mn oxide due to the synergistic effect of the coating Fe and Mn oxides. This research extended the potential applicability of FMBO to a great extent and provided a convenient approach to efficiently remove trace As(III) from water. (C) 2013 Elsevier Ltd. All rights reserved.

Size-dependent As(V) adsorption of reduced graphene oxide/magnetite nanocomposites

Fe-MOFs/graphene oxide-derived magnetic nanocomposite for enhanced adsorption of As(V) in aqueous solution

Preparation of Fe3O4/graphene oxide nanocomposites on activated carbon for As(V) removal from aqueous solutions

Zr-doped MIL-101(Fe)/Graphene oxide nanocomposites: An efficient and water-stable MOF-based adsorbent for As(V) adsorption in aqueous solution

Synthesis of CS-Fe 3 O 4 /GO nanocomposite for adsorption of heavy metal in aqueous environment

Fabrication of Fe3O4@GO@ZIF-8 nanohybrids via in-situ self-assembly with magnetic collectability for efficient adsorption of As(III) and As(V)

Removal of Arsenic Contaminants with Magnetic Γ-Fe2o3 Nanoparticles

Adsorption Behavior and Removal Mechanism of Arsenic on Graphene Modified by Iron–manganese Binary Oxide (femnox/rgo) from Aqueous Solutions

Removal of As(V) from aqueous solution using modified Fe3O4 nanoparticles

Adsorption behavior and mechanism of different arsenic species on mesoporous MnFe 2 O 4 magnetic nanoparticles.

Assessment of the adsorption capacity metal ions in wastewater of graphene oxide/ magnetite/chitosan materials

[Arsenic Adsorption by Magnetic Adsorbent CuFe2O4].

Evaluation of the colloidal stability and adsorption performance of reduced graphene oxide-elemental silver/magnetite nanohybrids for selected toxic heavy metals in aqueous solutions

A systematic study of arsenic adsorption and removal from aqueous environments using novel graphene oxide functionalized UiO-66-NDC nanocomposites

Synthesis of Iron Oxide Nanoparticle Functionalized Activated Carbon and Its Applications in Arsenic Adsorption

Efficient removal of As(III) via simultaneous oxidation and adsorption by magnetic sulfur-doped Fe-Cu-Y trimetal oxide nanoparticles

Efficient Removal of Trace Arsenite Through Oxidation and Adsorption by Magnetic Nanoparticles Modified with Fe-Mn Binary Oxide

Arsenic removal from aqueous solutions by adsorption onto iron oxide/activated carbon magnetic composite

Novel Insight into Adsorption and Co-Adsorption of Heavy Metal Ions and an Organic Pollutant by Magnetic Graphene Nanomaterials in Water

Graphene Oxide/cufe2o4 Foam As an Efficient Absorbent for Arsenic Removal from Water

Magnetic graphene oxide nanocomposite functionalized with glucamine for the trace extraction of arsenic (III) from aqueous media