A High Capacity p-Type Organic Cathode Material for Aqueous Zinc Batteries

Yan Zhang,Min Li,Zongyang Li,Yongyi Lu,Houmou Li,Jiaxin Liang,Xinyu Hu,Libin Zhang,Kun Ding,Qunjie Xu,Haimei Liu,Yonggang Wang

DOI: https://doi.org/10.1002/anie.202410342

2024-09-02

Abstract:P-type organic cathode materials typically exhibit high redox potentials and fast redox kinetics, presenting broad application prospects in aqueous zinc batteries (AZBs). However, most of the reported P-type organic cathode materials exhibit limited capacity (< 100 mAh g-1), which is attributable to the low mass content ratio of oxidation-reduction active functional groups in these materials. Herein, we report a high-capacity p-type organic material, 5,12-dihydro-5,6,11,12-tetraazatetracene (DHTAT), for aqueous zinc batteries. Both experiments and calculation indicate the charge storage of DHTAT involves the adsorption/ desorption of ClO4- on the -NH- group. Benefitting from the high mass content ratio of the -NH- group in DHATA molecule, the DHATA electrode demonstrates a remarkable capacity of 224 mAh g-1 at a current density of 50 mA g-1 with a stable voltage of 1.2 V. Notably, after 5000 cycles at a high current density of 5 A g-1, DHTAT retains 73% of its initial capacity, showing a promising cycling stability. In addition, DHTAT also has good low-temperature performance and can stably cycle at -40 °C for 4000 cycles at 1 A g-1, making it a competitive candidates cathode material for low-temperature batteries.