Optimize the surface morphology of dental implant on trans-gingival part with micro-pattern chip
CY Bao,MQ Wang,Q Zhang,GM Ou,P Gong
DOI: https://doi.org/10.3969/j.issn.1007-3957.2009.02.059
2009-01-01
Abstract:Purpose:Percutaneous-transmucosal devices refer to artifical devices remaining long-term in vivo and exercising specific function;this retention could be obtained by the means of through skin/gingiva or skin/mucosa.It has been widely applied to dental implant、maxillofacial prosthesis、percutaneous implanted prosthetics and etc.But this kind of devices exist certain failures in practical application.The major reasons are peri-implantitis and deficiency of satisfactory combination between soft tissue and implanted materials.The chemical composition and physical morphology of percutaneous-transmucosal position determine the adhesion of bacterial and soft tissue,and influence the hermetization between soft tissue and implanted materials.Referring to physical morphology,most scholars suggest the surface of the position should be relative smooth.However,it still remains unclear that which kind of morphological characteristics is helpful to biological seal for soft tissue.In order to explore and optimize the physical patterns which can achieve the goal of soft tissue biological seal for percutaneous-transmucosal,micrometer structure specimen was made under precise control.Then screening the structure which can influence the adhesion and proliferation of C2C12 、S.a and P.g.Method:A.The making of micrometer structure chips:Synthesis nanoHA slurries by wet heating treatment,and the HA disc with submicron range surface was made.The microstructure were divided into 23(400um×400um)areas,one of which was used as control and the others were fabricated with laser ablation as below:the sizes are 1um,3um,5um,10um respectively;the depths correspond with the size;the space are 10um,20um respectively;the shape are line,crosslock,round hole and triangle.The surface of HA microstructure chip were analyzed by XRD、SEM and Raman spectroscopy.Then we replicate with PDMS to get the same microstructure of nanoHA.The topography of the chips was observed by SEM.B.The adhesion and proliferation of C2C12 on microstructure chips:after defrostation and amplification,the cells were seeded on the HA specimen in 24 well culture plate at a density of 4×103 cells per well.For PDMS,the density is 4×104 cells per well.After culturing for 6h,1d,3d,5d respectively,the cells were stained with DAPI,and then observed under invert phase contrast microscope and laser scanning confocal microscope.C.The adhesion and proliferation of bacterial on microstructure chips:two kinds of bacterial were inoculated into PDMS in 24 well culture plate,For S.a,the inoculative numbers are 1×106/well,and for P.g,the numbers are 1×108/well.Bacterial were cultured for 24hours and 48hours respectively,The influence of microstructure chip on the adhesion of S.a and P.g was analyzed by SEM and the bacteria were quantitative counted according to SEM.Result:Z A.SEM showed the particulate size of calcium phosphate ceramics slurries was 60nm×250nm.XRD showed their chemical composition was pure HA.Submicron HA disc could be fabricated by nanoHA slurries.Various shapes of microstructure could be fabricated by laser ablation.XRD and Raman spectroscopy showed the chemical composition of ceramics was still pure HA.Chips with the same micro pattern of HA disc could be replicated by PDMS.B.C2C12 cells were seeded on specimen.The numbers of the cell adhered to the specimen became higher as the prolongation of cultivate time.But the adhesive and proliferation numbers varied in different micrometer structure domains,which indicated that the cells were easier to adhere to the microstructure domains in those with bigger space and smaller size,especially in the submicron regions with original scraggly crystal but not be artifically fabricated.Although cellular behavior on specimen(HA、PDMS)was different,they all manifested similar property on the same microstructure.C.The two kinds of bacterial could mainly adhere to the microstructure,and the adhesive bacterial number was directly proportional to the number and the width of the grooves but had no significant relationship with microstructure shape.For those materials with submicron regions,less adhesion took place.Conclusion:A.NanoHA slurries were firstly adopted to fabricate ceramics composed of submicron and micrometer structure was made on ceramics by laser ablation.Then the same microstructure was replicated on PDMS.These structures worked as a foundation for the next high throughput screening which can analyze the influence of the microstructure on the behaviors of cells and bacteria.B.Cells were inclined to be adhered and proliferate in submicron regions,whereas bacteria were inclined to be adhered and proliferate in microstructure regions,but not submicron regions,This result could provide preliminary theory and basis for exploring and optimizing physical pattern in percutaneous-transmucosal devices.