Abstract:In this study, a series of Cu–Ti3SiC2 composites with different Ti3SiC2 contents were prepared by spark plasma sintering. Their mechanical properties and electrical resistivity were investigated. Through analyzing the morphology and composition of the eroded regions, the effect of Ti3SiC2 content on the erosion behavior of Cu–Ti3SiC2 cathodes under vacuum arc was studied. Results show that the relative density and bending strength of the Cu–Ti3SiC2 composites decrease with the increasing Ti3SiC2 content, while the opposite holds for hardness and electrical resistivity. The morphology and phase composition of the erosion zone is dominated by the decomposition process and the amount of Ti3SiC2 in the cathode. Cu–Ti3SiC2 cathodes containing 10 mass%Ti3SiC2 or less displayed relatively flat eroded surface morphology. Cathodes with high Ti3SiC2 content suffered more serious erosion with voids, cracks, and severe decomposition of Ti3SiC2, all of which contribute to impairing the arc ablation resistance of the composite. Ti3SiC2 particles decomposed into TiC and Si vapor; eventually, this TiC also decomposed into Ti vapor and C, leaving a considerable amount of C on the arc affected cathode surface. Excess addition of Ti3SiC2 particles not only deteriorates the strength but also the electrical and thermal conductivity of the composite, both of which in turn harms the arc erosion resistance of the material. These results suggest that the optimal Ti3SiC2 content is below 10 mass% in the composite.

Electrochemical Corrosion Behavior and the Related Mechanism of Ti3SiC2/Cu Composites in a Strong Acid Environment

Corrosion behaviors of Ti3SiC2/Cu in dilute HNO3 and concentrated H2SO4 and its corrosion mechanism

Electrochemical Corrosion Behaviors of Ti3SiC2/Cu Composites in a 3.5% NaCl Solution

Corrosion behaviors of Ti3SiC2/Cu composites in molten salts

Corrosion Behavior of Porous Ti3SiC2 in Nitric Acid and Aqua Regia

Corrosion behavior and mechanism of Cu/Ti3AlC2 composites under arc discharge in different atmospheres

Corrosion behavior of Ti2Ni3Si/NiTi intermetallic alloys in H2SO4 solution

Arc Erosion Behavior and Mechanism of Cu/Ti3SiC2 Composites in C-C4f8/co2 and C-C4f8/n2 Mixtures

Corrosion Resistance of Porous Ti3(Si,Al)C2 Intermetallics in Hydrochloric Acid Solution

Influence of Ti3SiC2 content on erosion behavior of Cu–Ti3SiC2 cathode under vacuum arc

Corrosion Behaviors and Mechanism of Electroless Ni-Cu-P/n-TiN Composite Coating

Corrosion Behavior Ofin-Situtib2/7050al Composite in NaCl Solution at Different Ph Values

(Digital Presentation) Corrosion-Resistance Investigation of Titanium Passive Layer in Acidic Solution

Electrochemical Behavior and Corrosion Protection Performance of Bis[Triethoxysilylpropyl] Tetrasulfide Silane Films Modified with Tio2 Sol on 304 Stainless Steel

Corrosion Behavior of WC–10 Wt % Ni3Al Composite in Acidic Media

Corrosion Behavior of Nanostructured Ni‐Si3N4 Composite Films: A Study of Electrochemical Impedance Spectroscopy

Improving Corrosion Resistance of Ti Alloy in Hydrochloric Acid by Embedding TiC/TiB and Y2O3 Ceramic Nano-Particles

Electrochemical corrosion of Ti-Si-N films coated by pulsed-DC plasma enhanced CVD

Corrosion properties and mechanism of Ti43Zr27Mo5Cu10Be15 amorphous composites in various conditions

(Digital Presentation) Anti-Corrosion Investigation of Titanium Electrode for Cu Plating

Electrochemical corrosion behavior of micrometer-sized porous Ti<sub>3</sub>SiC<sub>2</sub> compounds in NaCl solution