MXene enhanced reduced graphene oxide aerogel for high-performance supercapacitors

Zhenjiang Wang,Xinli Yang,Gang Wang,Xiping Yang,Longhao Qiao,Mingxia Lu

DOI: https://doi.org/10.1063/5.0219584

2024-08-21

Abstract:Three-dimensional (3D) reduced graphene oxide (rGO)/Ti2CTx MXene hybrid aerogels were effectively prepared by a two-step method involving hydrothermal reaction and freeze-drying. The intimately coupled rGO/Ti2CTx hybrid aerogel combined high electrical conductivity, large interlayer spacing, and excellent mechanical stability of Ti2CTx, which not only effectively prevents the self-restacking of Ti2CTx nanosheets, exposes more active sites exposed, and improves the volume change during the charge/discharge process but also increases the accessibility of ions and promotes the rapid transfer of ions/electrons. As a result, rGO/Ti2CTx 17.5-2.5 as the working electrode of electric double layer capacitors delivers a large specific capacity (107.05 F g-1 at 0.5 A g-1 in a 1M Na2SO4 electrolyte), a high rate capability (maintains 30% of its initial capacitance at 10 A g-1, which is much better than rGO and Ti2CTx), and excellent long-term large-current cycle stability (the initial capacitance remains above 71.1% after 10 000 cycles at 1 A g-1). In addition to providing a high-performance electrode for supercapacitors, this study proposes an efficient and time-saving strategy for constructing 3D structures from 2D materials.