Fabrication and TA@MOF-808 modification of new thin-film composite membranes for effective retrieval of ionic rare earths
Zhaohuang Zhong,Xindong Li,Siwei Yu,Jianghui Jia,Jiaju Huang,Meng Cai,Qinyan Zhu,Luo Bao,Wanfu Huang
DOI: https://doi.org/10.1016/j.seppur.2024.127357
IF: 8.6
2024-04-27
Separation and Purification Technology
Abstract:Retrieval of rare earth ions from dilute wastewater produced from in-situ leach mining is a crucial approach to effectively mitigate the shortage of rare earth resources, and the employment of the membrane technology for recuperation of ionic rare earths is an energy-efficient and eco-friendly solution. In this study to optimize the use of the membrane technology for ionic rare earths recovery, TA@MOF-808 was fabricated by combining tannic acid (TA) with MOF-808 and then incorporated as nanoparticles into a polyetherimide (PEI) base membrane. On this basis, PA/PEI-TA@MOF-808 thin-film composite membranes were prepared via interfacial polymerization. TA@MOF-808 with its hydroxyl and carboxyl functional groups generated hydrogen and covalent bonds with the secondary amine groups of piperazine (PIP), which stored PIP and regulated its diffusion rate into the organic phase. Thereby, the membrane surface charge was modulated under acidic conditions, and a separation layer was reconstituted, improving the structural and operational stability of the membranes. The PA/PEI-TA@MOF-808 membrane exhibited a water flux of 42.1 L·m −2 ·h −1 , and La 3+ , Y 3+ , and Gd 3+ retention rates of 97.7 %, 96.7 % and 97.4 %, respectively. Separation tests, acid resistance tests, long-term operational stability tests and actual rare earth wastewater treatment tests revealed the PA/PEI-TA@MOF-808 membrane possessed outstanding ionic rare earth separation capability, consistent membrane flux, notable acid resistance, and operational stability, suggesting a bright future in the application for ionic rare earth recovery.
engineering, chemical