Abstract:Na3V2(PO4)3 (NVP) has been deemed to be a prospective cathode for sodium ion batteries (SIBs) duo to its high structural stability and flat voltage platform. Herein, a series of K/Co co-doped NVP composites with optimized sodium storage property are produced via a feasible sol-gel method. Significantly, the introduced K+ has substituted of Na+ at Na1 site, strictly demonstrated by the Rietveld refinement results. Meanwhile, this substitution has hardly influence on the reversible de/insertion of Na+ situated at Na2 site. Moreover, the beneficial K+ with larger ionic radius can act as the pillar ion to improve the structural stability efficiently. Furthermore, the replacement of V3+ by Co2+ facilitates to enlarging the interplanar spacing in crystal structure, resulting in accelerating the Na+ migration effectively. Moreover, substitution with low valence element (Co2+ vs. V3+) can generate the favorable holes to increase the intrinsic electronic conductivity. Notably, doping with appropriate content of K/Co elements favors to reduce the particle size and shorten the pathway for Na+ transformation, distinctly boosting the apparent ionic diffusivity. Specifically, K/Co co-doping induces to forming the unique mesoporous morphology, immensely enlarging the specific surface area of active grains and therefore facilitating the infiltration between the particles and electrolyte. Comprehensively, the optimized K0.1Co0.05-NVP/C exhibits an outstanding electrochemical performance. It shows a high initial capacity of 122.7 mA h g−1 at 0.1 C, which is higher than the theoretical value of NVP (117.6 mA h g−1). It can release an initial capacity of 100.9 mA h g−1 at 1 C and maintain 71.0 mA h g−1 after 500 cycles. Moreover, the reversible capacity can be achieved as 98.8 mA h g−1 at a high rate of 10 C and a favorable retention of 75.9% can be obtained after 400 cycles. Besides, the kinetic characteristics for the modified K0.1Co0.05-NVP/C cathode are superior than those of pristine NVP/C. Specifically, it reveals a relatively high diffusion coefficient of Na+ (0.53 × 10−10 cm2 s−1). Thus, the modified K/Co co-doped NVP/C sample can be a promising cathode material for SIBs.

Microstructure tuned Na3V2(PO4)3@C electrodes toward ultra-long-life sodium-ion batteries

Carbon-Decorated Na3V2(PO4)3 As Ultralong Lifespan Cathodes for High-Energy-Density Symmetric Sodium-Ion Batteries.

Citric acid-assisted synthesis of Na3V2(PO4)3/C composite as high-performance electrode material for sodium-ion batteries

A robust carbon coating of Na3V2(PO4)3 cathode material for high performance sodium-ion batteries

Nanoconfined Carbon‐Coated Na3V2(PO4)3 Particles in Mesoporous Carbon Enabling Ultralong Cycle Life for Sodium‐Ion Batteries

Carbon-Coated Na3v2(Po4)(3) Anchored on Freestanding Graphite Foam for High-Performance Sodium-Ion Cathodes

3D interconnected porous carbon coated Na3V2(PO4)3/C composite cathode materials for sodium-ion batteries

Constructing Micro-Nano Na3V2(PO4)3/C Architecture for Practical High-Loading Electrode Fabrication As Superior-Rate and Ultralong-Life Sodium Ion Battery Cathode

Na 3 V 2 (PO 4 ) 3 @nitrogen,sulfur-codoped 3D porous carbon enabling ultra-long cycle life sodium-ion batteries.

Construction of Three-Dimensional Electronic Interconnected Na3V2(PO4)3/C As Cathode for Sodium Ion Batteries

Diatomic Doped Carbon Coating Boosting the High-Rate Performance and Super Long-Cycle Stability of Na3v2(Po4)3 Cathode Material

NASICON-Type Na 3 V 1.5 Cr 0.4 Fe 0.1 (PO 4 ) 3 : High-Voltage and High-Rate Cathode Materials for Sodium-Ion Batteries

Highly Reversible Na Storage in Na3V2(PO4)3 by Optimizing Nanostructure and Rational Surface Engineering

High-rate performance and super long-cycle stability of Na3V2(PO4)3 cathode material coated by diatomic doped carbon

Boosting the rate capability and working lifespan of K/Co co-doped Na3V2(PO4)3/C for sodium ion batteries

Preparation of Na3V2(PO4)3 Cathode Materials by Hydrothermal Assisted Sol-Gel Method for Sodium -Ion Batteries

One–Step Synthesis of Three–Dimensional Na3V2(PO4)3/Carbon Frameworks as Promising Sodium–Ion Battery Cathode

Micro/Nano Na3V2(PO4)3/N-Doped Carbon Composites with a Hierarchical Porous Structure for High-Rate Pouch-Type Sodium-Ion Full-Cell Performance

Na3V2(PO4)3 Coated by N-doped Carbon from Ionic Liquid As Cathode Materials for High Rate and Long-Life Na-ion Batteries

Design and Construction of 3D Porous Na3V2(PO4)3/C as High Performance Cathode for Sodium Ion Batteries

One‐Dimensional Na3V2(PO4)3/C Nanowires As Cathode Materials for Long‐Life and High Rate Na‐Ion Batteries