Abstract:High-performance Co-based catalysts were derived by pyrolysis using synthesized MOFs as self-sacrificial templates. Various catalytic systems were constructed by peroxymonosulfate (PMS) to degrade tetracycline hydrochloride (TC). Adsorption-degradation efficiencies, cycle performance, dynamics, and the adsorption catalytic mechanism of various catalytic systems for TC were studied. The effects of different synthetic solvents, pyrolysis temperatures, and single/bimetallic element compositions on degradation efficiency were innovatively compared. The optimal catalyst and PMS dosage for the experiment were determined to be 10 mg and 0.1 mL, respectively. The results indicated that all catalytic systems could efficiently degrade TC and have a high acid-base resistance. The catalyst activity was significantly influenced by the pyrolysis temperature. The optimum pyrolysis temperatures for Zn@Co-N-C-T, CH3OH@Co-N-C-T, and H2O@Co-N-C-T were 1000, 900 and 900 °C, respectively. More abundant pore structures and active sites were generated in Zn@Co-N-C-1000, exhibiting an excellent TC degradation efficiency and adsorption capacity, achieving 94.73% and 167.564 mg/g, respectively. Meanwhile, the total organic carbon (TOC) of TC (50 mL, 50 mg/L) achieved a removal rate (TOC/TOC0) of 50.28%. Zn@Co-N-C-1000/PMS maintained over 83.27% TC degradation after five cycles. The adsorption mechanism of the catalyst for TC was investigated through the analysis of adsorption kinetics and isotherm models. The quenching test and EPR results indicated that TC was primarily degraded through the nonradical pathway. The efficient degradation of TC is attributed to the rapid electron transfer processes occurring at the two-phase interface and the redox cycling of Co0/Co2+/Co3+. Finally, LC-MS was used to analyze the intermediate products of TC degradation in the Zn@Co-N-C-1000/PMS system, and two degradation pathways were proposed.

Cu-Co bimetallic organic framework as effective adsorbents for enhanced adsorptive removal of tetracycline antibiotics

Adsorption characteristics of tetracycline hydrochloride and oxytetracycline by a MOF-525(Co) metal organic framework

Bimetallic Fe/Co-MOFs for tetracycline elimination

Magnetic porous carbons derived from metal-organic frameworks for effective adsorption of tetracycline

Hollow Co3S4 polyhedron decorated with interlayer-expanded MoS2 nanosheets for efficient tetracycline removal from aqueous solution

Heterogeneous nucleation and synthesis of carbon dots hybrid Zr-based MOFs for simultaneous recognition and effective removal of tetracycline

Highly efficient removal of tetracyclines from water by a superelastic MOF-based aerogel: Mechanism quantitative analysis and dynamic adsorption

Fabrication of magnetic trimetallic metal-organic frameworks for the rapid removal of tetracycline from water

Bismuth (III)-based metal-organic framework for tetracycline removal via adsorption and visible light catalysis processes

Preparation of NH2-MIL-101(Fe) Metal Organic Framework and Its Performance in Adsorbing and Removing Tetracycline

Preparation of bimetallic metal–organic frameworks for adsorbing doxycycline hydrochloride from wastewater

Cobalt Iron-Metal Organic Framework Coordinated to CMC Aerogel by Solvothermal Method and Application to Tetracycline Antibiotics Adsorption

Effective and structure-controlled adsorption of tetracycline hydrochloride from aqueous solution by using Fe-based metal-organic frameworks

Effective Removal of Tetracycline from Water Using Copper Alginate @ Graphene Oxide with In-Situ Grown MOF-525 Composite: Synthesis, Characterization and Adsorption Mechanisms

Bimetal doped Cu-Fe-ZIF-8/g-C3N4 nanocomposites for the adsorption of tetracycline hydrochloride from water

Enhanced adsorption and synergistic photocatalytic degradation of tetracycline by MOF-801/GO composite via solvothermal synthesis

Efficient Adsorption and Degradation of Tetracycline Hydrochloride Using Metal-Organic Framework-Derived Cobalt-Based Catalysts and Mechanism Insight

Fabrication of dual-functional Zr-based MOF incorporating amino and sulfoxide derivatives for simultaneous removal and detection of tetracycline antibiotics

Simultaneously efficient adsorption and photocatalytic degradation of tetracycline by Fe-based MOFs.

Adsorption performance and optimization by response surface methodology on tetracycline using Fe-doped ZIF-8-loaded multi-walled carbon nanotubes

Adsorption and Removal of Antibiotic Pollutants using CuO-Co<sub>3</sub>O<sub>4</sub> Co-modified Porous Boron Nitride Fibers in Aqueous Solution