Additive‐Free, Low‐Temperature Crystallization of Stable α‐FAPbI 3 Perovskite
Tian Du,Thomas J. Macdonald,Ruo Xi Yang,Meng Li,Zhongyao Jiang,Lokeshwari Mohan,Weidong Xu,Zhenhuang Su,Xingyu Gao,Richard Whiteley,Chieh‐Ting Lin,Ganghong Min,Saif A. Haque,James R. Durrant,Kristin A. Persson,Martyn A. McLachlan,Joe Briscoe
DOI: https://doi.org/10.1002/adma.202107850
IF: 29.4
2022-01-23
Advanced Materials
Abstract:Formamidinium lead triiodide (FAPbI<sub>3</sub> ) is attractive for photovoltaic devices due to its optimal bandgap at around 1.45 eV and improved thermal stability compared with methylammonium-based perovskites. Crystallization of phase-pure α-FAPbI<sub>3</sub> conventionally requires high-temperature thermal annealing at 150 °C whilst the obtained α-FAPbI<sub>3</sub> is metastable at room temperature. Here, aerosol-assisted crystallization (AAC) is reported, which converts yellow δ-FAPbI<sub>3</sub> into black α-FAPbI<sub>3</sub> at only 100 °C using precursor solutions containing only lead iodide and formamidinium iodide with no chemical additives. The obtained α-FAPbI<sub>3</sub> exhibits remarkably enhanced stability compared to the 150 °C annealed counterparts, in combination with improvements in film crystallinity and photoluminescence yield. Using X-ray diffraction, X-ray scattering, and density functional theory simulation, it is identified that relaxation of residual tensile strains, achieved through the lower annealing temperature and post-crystallization crystal growth during AAC, is the key factor that facilitates the formation of phase-stable α-FAPbI<sub>3</sub> . This overcomes the strain-induced lattice expansion that is known to cause the metastability of α-FAPbI<sub>3</sub> . Accordingly, pure FAPbI<sub>3</sub> p-i-n solar cells are reported, facilitated by the low-temperature (≤100 °C) AAC processing, which demonstrates increases of both power conversion efficiency and operational stability compared to devices fabricated using 150 °C annealed films.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology