Preosteoblast Adhesion and Viability Study of Freeze-Dried Bovine Bone Block Scaffold Coated with Human Umbilical Cord Mesenchymal Stem Cell Secretome

Arum Nur Kartika Putri,David Buntoro Kamadjaja,Andra Rizqiawan,Muhammad Subhan Amir,Ni Putu Mira Sumarta,Dewi Kartikawati Paramita

DOI: https://doi.org/10.1055/s-0044-1787105

2024-07-16

Abstract:Objectives: Combining a three-dimensional scaffold with growth factors before implantation is one method used to increase scaffold bioactivity in bone tissue engineering. The mesenchymal stem cell (MSC)-conditioned medium (CM), called secretome, contains many proteins and growth factors required for tissue repair and growth. This study evaluated the bioactivity of a bovine bone scaffold combined with the secretome of human umbilical cord MSCs (hUC-MSCs) by analyzing MC3T3-E1 cell adhesion and viability on the scaffold. Materials and methods: This in vitro laboratory study evaluated the effect of hUC-MSC secretome applied to bovine bone scaffolds processed using various techniques on MC3T3-E1 cell adhesion and viability. The three experimental groups included deproteinized bovine bone mineral-secretome (DBBM-CM), freeze-dried bovine bone-secretome (FDBB-CM), and decellularized FDBB-CM, whereas the control group was treated with DBBM alone. The cell adhesion test was performed using the centrifugation method after 6 and 24 hours, whereas the cell viability test was conducted using the trypan blue exclusion method after 24, 48, and 72 hours. Cell attachment was visualized after 4',6-diamidino-2-phenylindole staining and viewed under inverted fluorescence microscopy. Stastical analysis: Statistical analyses were performed using one-way analysis of variance, followed by a post hoc test in cases of significant differences. Results: Statistical analyses showed significantly greater adhesion of the preosteoblasts to the FDBB-CM scaffold at 6 hours (p = 0.002). The results of the adhesion test at 24 hours and the viability tests at all observation times showed no significant differences (p > 0.05). This study found that the average MC3T3-E1 cell adhesions and viabilities were highest for the FDBB-CM and DBBM-CM scaffolds. DBBM scaffolds with the secretome had better cell adhesion and viability than those without the secretome. Conclusion: The addition of MSC secretome increased bovine bone scaffold bioactivity especially in DBBM and FDBB scaffolds.