Abstract:Nitrided steel is being used to increase the lifetime and wettability of selective soldering nozzles. In this environment, the liquid solder wets to the surface of the nozzle to enable control of the solder flow during the soldering process. Pre-treatment is a key step in the processing of parts for electroplating. Pre-treatment usually involves degreasing and acidic pickling steps in order to remove adsorbed oil-based compounds and oxides respectively. These steps ensure a well-structured and adherent electroplated coating to the part. Surface treatments such as nitriding alter the surface composition of steels and thereby change the conductivity/surface activity. Typically, a nitrided surface contains a dual-phase surface layer followed by a diffusion zone consisting of the formed nitrides and finally a transition zone to the bulk material. Generally, this surface treatment is performed to harden materials without the risk of dimensional changes. For a selective soldering application, it reduces the dissolution of material into the solder during operation while also improving the wetting of the nozzle. The electroplated coatings for the selective soldering nozzles consist of 10 microns of nickel and 10 microns of tin. This structure allows for near-instant wetting and use of the nozzle. Furthermore, the electroplated layers provide corrosion protection for the nozzle ensuring no oxide or scale layers will form that may require flux for cleaning. A range of chemical and electrochemical pre-treatment steps were explored to prepare and optimally activate the nitride-hardened steel surfaces for electroplating. The processes included: hot degreasing and electrolytic degreasing with alkaline detergents; electrolytic descaling in a solution containing sodium hydroxide; chemical pre-descaling process with potassium permanganate; varying the compositions of pickling in inorganic acids; different formulations for nickel strike electrolytes for plating onto ferrous alloys. Mass loss measurements provided an estimation of the thickness of the material removed due to acid pickling. Scanning electron microscopy was employed to assess changes in the surface due to the pre-treatment. Open circuit potential measurements were applied to measure the surface activity before any pre-treatment and also the change in surface conductivity/activity post-treatment. Nanoindentation measurements were used to assess the change in surface hardness as a result of the nitriding treatment and also to check for the presence of the remaining hardened nitrided layer after pre-treatment. Glow discharge optical emission spectroscopy was utilised to study the elemental depth profile of the nitrided parts. Crystalline structure was studied through x-ray diffraction. After pre-treatment, a Woods nickel strike was applied to prepare the surface for further electroplating with bright tin. SEM analysis of the cross-sections of the coated specimens was used to analyse the coating microstructure. Thickness of the electrodeposited coatings were confirmed with x-ray fluorescence. Thermal shock tests were performed to confirm that the adhesion of the coating was sufficient. Approximately half of the nitrided layer was removed by pre-treatment in order to activate the surface for electroplating. More severe pre-treatment was required compared to electroplating non-hardened parts to activate the surface. Surface conductivity/surface activity was altered as measured by OCP resulting from the pre-treatment. This work has analysed the surface modification of nitride-hardened steels during the pre-treatment steps required to initiate electroplating and has shown that it is possible to prepare nitride-treated steels for electroplating. The results can be used to develop more optimal pre-treatment processes for electroplating nitrided steels.

Increasing the Wear Resistance of Structural Steel Parts by Ion Nitriding during Complex Surface Preparation Using the Dry Electropolishing Method

On issue of selecting of ion implantation dose for activating of surface layer of alloy steel parts before nitriding

Solutions to improve surface hardness of stainless steels without loss of corrosion resistance

Effect of Plasma Nitriding Pretreatment on the Mechanical Properties of AlCrSiN-Coated Tool Steels

Enhancing Heavy Load Wear Resistance of AISI 4140 Steel Through the Formation of a Severely Deformed Compound-Free Nitrided Surface Layer

Surface Modification of Chromium–Nickel Steel by Electrolytic Plasma Nitriding Method

Effect of Gas and Ion Plasma Nitriding on the Structure and Properties of Forging Die Inserts

Short Time Ion Nitriding of AISI 420 Martensitic Stainless Steel to Improve Wear and Corrosion Resistance

Friction and Wear Behavior of Duplex-Treated AISI 316L Steels by Rapid Plasma Nitriding and (crwaltisi)n Ceramic Coating

Electrolytic Plasma Nitriding of Medium-Carbon Steel 45 for Performance Enhancement

Improvement of nitrogen ion implantation on the wear and corrosion resistance of bearing steel in NaCl solution

Enhancement of surface properties of 45# carbon steel using plasma immersion ion implantation

Effect of Electric Potentials on Microstructure, Corrosion and Wear Characteristic of the Nitrided Layer Prepared on 2cr13 Stainless Steel by Plasma Nitriding

Analysis of Pre-Treatment Processes to Enable Electroplating on Nitrided Steel

Surface Texturing-Plasma Nitriding Duplex Treatment for Improving Tribological Performance of AISI 316 Stainless Steel

Improved Mechanical Properties, Wear and Corrosion Resistance of 316L Steel by Homogeneous Chromium Nitride Layer Synthesis Using Plasma Nitriding

Plasma Nitriding of AISI 304 Stainless Steel in Cathodic and Floating Electric Potential: Influence on Morphology, Chemical Characteristics and Tribological Behavior

Low energy, high current density ion implantation of materials at elevated temperatures for tribological applications

Effect of Dose Rate on Tribological Properties of 8Cr4Mo4V Subjected to Plasma Immersion Ion Implantation

Tribological Behaviors of Steel Surfaces Treated with Ion Sulphurization Duplex Processes

Process Window and Mechanism of Surface Property Enhancement of 9cr18 Steel Using Plasma Immersion Ion Implantation