Abstract:Abstract Fabrication of surfaces with hydrophobic and superhydrophobic property has drawn extensive interests as a solution to protect metal surfaces from corrosion attacks, with potential applications in cooling devices for electronics, microfluidic systems for controlled drug delivery, as well as anti-icing, and self-cleaning techniques. This study addresses the impact of surface wettability, i.e., hydrophobicity and superhydrophobicity, on corrosion resistance improvement of metal materials. Hydrophobic and superhydrophobic metal surfaces are desirable to minimize the adhesion between water droplets and the surface. This study aims to fabricate and investigate 17-4 PH stainless steel surfaces with lowered surface energies and modified wetting properties. Various micro- and sub-micro scale finished surfaces with different surface roughness, namely as-received, sandblasted, ground, and polished, were employed, followed by applying a low energy superhydrophobic coating to fabricate hydrophobic and superhydrophobic surfaces on 17-4 PH stainless steel base material. The specific impacts of the surface roughness on wettability and corrosion resistivity of the manufactured surfaces were examined. The ground and polished surfaces followed by applying a 30–50 μm thick superhydrophobic dip coating resulted in steady-state contact angles of up to 152° and 146°, respectively, while the non-engineered coated base metal exhibited the contact angle of 140°. The ground surface with the average surface roughness (Ra) of ∼ 0.03 μm has the optimal roughness. According to the Cassie-Baxter model, the coated ground surface can retain the entrapped air within its interstices more adequately than the other surfaces with either lower surface roughness, such as the polished surface with the roughness of 0.02 μm, or higher surface roughness, such as as-received and sandblasted surfaces with the Ra value of 5.52 μm and 11.98 μm, respectively. To study the corrosion performance and electrochemical stability of the fabricated surfaces, cyclic polarization testing (CPT) and electrochemical impedance spectroscopy (EIS) were performed in an aerated 3.5 wt.% NaCl solution that mimics seawater environment. The electrochemical measurements confirmed that the water-repelling property of the surface contributes to the anti-corrosion capability of the substrate. Data from the corrosion tests indicate that the lowest corrosion current density, highest corrosion potential, and highest pitting potential, were found for the coated ground surface followed by the coated polished surface. The EIS results also highlighted the significantly greater absolute value of impedance for the coated ground and coated polished surfaces even after 240 hrs of immersion in the electrolyte solution than the other fabricated surfaces at lower frequency ranges. The improvement in the 17-4 PH stainless steel corrosion performance was contributed to the size of the fabricated surface micro- and sub-micro scale features, capable of retaining the entrapped air within the roughened surface structure when fully immersed in a corrosive environment. This work demonstrates the effectiveness of a simple fabrication process to create hydrophobic and superhydrophobic stainless steel surfaces with improved corrosion resistivity.

Effect of etching duration on roughness and wettability of different carbon steel substrates

Effect of Pre-treatment on Roughness and Hydrophobicity of Electro-Etched Steel with Improved Corrosion Resistance

A wear-resistant superhydrophobic surface on Q235 steel prepared by electrospark deposition and electrochemical etching

Fabrication and coating adhesion study of superhydrophobic stainless steel surfaces: The effect of substrate surface roughness

Fabrication and Corrosion Performance of a Superhydrophobic Stainless Steel Surface

Do Wettability Measurements Define Corrosion Inhibition of Etched Surfaces? A Study on Acid‐Etched 316L Stainless Steel

Effects of Chemical Etching on Surface Structure and Tribological Behavior of Silicate Substrates

Enhancing the wettability for 4043 aluminum alloy on 301L stainless steel via chemical-etched surface texturing

Effect of Surface Roughness of 316 L Stainless Steel Substrate on the Morphological and Super-Hydrophobic Property of TiO2 Thin Films Coatings

Superhydrophobicity on AISI 304 Stainless Steel through Surface Sensitization Process and Etching

Fabrication of cerium myristate coating for a mechanochemically robust modifier-free superwettability system to enhance the corrosion resistance on 316L steel by one-step electrodeposition

Effect of Surface Roughness on Contact Angle Measurement of Nanofluid on Surface of Stainless Steel 304 by Sessile Drop Method

Creation of Superhydrophobic Stainless Steel Surfaces by Acid Treatments and Hydrophobic Film Deposition

Mechanical, chemical and wetting properties of a superhydrophobic surface based on functionalized ZrO2 on stainless steel

Effect of Impact Angle and Speed, and Weight Abrasive Concentration on AISI 1015 and 304 Steel Exposed to Erosive Wear

A novel method to prepare superhydrophobic, UV resistance and anti-corrosion steel surface

Surface Characterization of Stainless Steels Prepared with Various Surface Treatments

The Influence of Adventitious Carbon Groups on the Wetting of Copper: A Study on the Effect of Microstructure on the Static Contact Angle

Wettability Behaviour of Metal Surfaces after Sequential Nanosecond and Picosecond Laser Texturing

Assessment of roughness and chemical modification in determining the hydrophobic properties of metals

A Study on the Wettability of Ion-Implanted Stainless and Bearing Steels