Ultrathin Densified Carbon Nanotube Film with “Metal-like” Conductivity, Superior Mechanical Strength, and Ultrahigh Electromagnetic Interference Shielding Effectiveness
Yan-Jun Wan,Xiao-Yun Wang,Xing-Miao Li,Si-Yuan Liao,Zhi-Qiang Lin,You-Gen Hu,Tao Zhao,Xiao-Liang Zeng,Chun-Hong Li,Shu-Hui Yu,Peng-Li Zhu,Rong Sun,Ching-Ping Wong
DOI: https://doi.org/10.1021/acsnano.0c06971
IF: 17.1
2020-10-12
ACS Nano
Abstract:Flexible and lightweight high-performance electromagnetic interference shielding materials with minimal thickness, excellent mechanical properties, and outstanding reliability are highly desired in the field of fifth-generation (5G) communication, yet remain extremely challenging to manufacture. Herein, we prepared an ultrathin densified carbon nanotube (CNT) film with superior mechanical properties and ultrahigh shielding effectiveness. Upon complete removal of impurities in pristine CNT film, charge separation in individual CNTs induced by polar molecules leads to strong CNT–CNT attraction and film densification, which significantly improve the electrical conductivity, shielding performance, and mechanical strength. The tensile strength is up to 822 ± 21 MPa, meanwhile the electrical conductivity is as high as 902,712 S/m, and the density is only 1.39 g cm<sup>–3</sup>. Notably, the shielding effectiveness is over 51 dB with a thickness of merely 1.85 μm in the broad frequency range of 4–18 GHz, and it reaches to ∼82 dB at 6.36 μm and ∼101 dB at 14.7 μm, respectively. Further, such CNT film exhibits excellent reliability after an extended period in strong acid/alkali, high temperature, and high humidity. It demonstrates the best overall performance among representative shielding materials by far, representing a critical breakthrough in the preparation of shielding film toward applications in wearable electronics and 5G communication.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.0c06971?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.0c06971</a>.Figures S1and S2 display the morphology of CNT film. Figure S3 shows the schematic of densification mechanism. Figures S4 and S5 show the results of XPS, FI-IR, EDS mapping, and thickness measurements of CNT films. Figure S6 shows the EMI shielding performance, electrical conductivity, and reliability of shielding films. Figures S7 and Figure S8 display the stress–strain curves of CNT films and flexibility. Figure S9 shows the test setup of magnetic probe method for near-field shielding effectiveness. Tables S1 and S2 list the physical properties and mechanical properties of CNT films. Tables S3 and S4 list the comparison of shielding performance with reported literatures (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.0c06971/suppl_file/nn0c06971_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology