A Non-Negligible Interface Effect for Alkaline Hydrogen Oxidation Reaction
Tonghui Zhao,Mingxing Gong,Deli Wang
DOI: https://doi.org/10.1149/ma2019-02/36/1665
2019-01-01
ECS Meeting Abstracts
Abstract:In alkaline medium, the slow kinetics of the anodic hydrogen oxidation reaction (HOR) hinders the development of alkaline membrane fuel cells (AMFCs). Therefore, it is of great significance to explore the mechanism of HOR from establishing the "structure-activity relationship" and researching the main factor influencing the activity of the catalyst. Generally accepted viewpoint is the hydrogen binding energy (HBE) theory, a main descriptor of the catalytic activity, and regulation of the binding energy usually could be achieved by controlling the lattice strain. In our research, by taking advantage of the difference in the atomic radius of the 3d transition metals, a trimetal model (Pd3M@Pt (M=Fe, Co, Cu) core-shell structure) is constructed to study the HOR through the tuning of stress shrink degrees. By step-by-step electrochemical monitoring method and surface-controlled technology, the phase changes in the cycle were regulated and analyzed. Interestingly, it shows that the low-valence M(OH)x species formed in the electrochemical cycle obviously influenced the HOR activity rather than the HBE change caused by lattice shrink, mainly ascribed to strengthen the adsorption of OHad species and accelerate the Volmer step (Had+OH-→H2O+e-+*, rate-determined step, RDS). Meanwhile, It's worth noting the mass activity (MA) and specific activity (SA) of Pd3Co@Pt are significantly improved compared with Pt/C, close to 4 and 2 times. This Pd3M@Pt core-shell structure also improves the utilization of Pt and facilitates the design of efficient HOR catalyst. Figure 1. a) Schematic diagram of the mechanism exploration for HOR with the model of Pd3M@Pt (M=Fe, Co, Cu); b) CV curves of four core-shell structure catalysts Keywords: Hydrogen Oxidation Reaction, Pd3M@Pt core-shell structure, low-valence M(OH)x species, interface effect References: Strmcnik D, Uchimura M, Wang C, et al. Nat. Chem., 2013, 5(4): 300. Lu S, Zhuang Z. J. Am. Chem. Soc., 2017, 139(14): 5156-5163. Li J, Ghoshal S, Bates M K, et al. Angew. Chem. Int. Edit., 2017, 56(49): 15594-15598. Figure 1