Room-temperature Hydrogenation of Halogenated Nitrobenzenes over Metal—organic-Framework-derived Ultra-Dispersed Ni Stabilized by N-doped Carbon Nanoneedles
Yuemin Lin,Yuanyuan Zhang,Renfeng Nie,Kai Zhou,Yao Ma,Mingjie Liu,Dan Lu,Zongbi Bao,Qiwei Yang,Yiwen Yang,Qilong Ren,Zhiguo Zhang
DOI: https://doi.org/10.1007/s11705-022-2220-9
IF: 4.803
2022-01-01
Frontiers of Chemical Science and Engineering
Abstract:Ultra-dispersed Ni nanoparticles (7.5 nm) on nitrogen-doped carbon nanoneedles (Ni@NCNs) were prepared by simple pyrolysis of Ni-based metal–organic-framework for selective hydrogenation of halogenated nitrobenzenes to corresponding anilines. Two different crystallization methods (stirring and static) were compared and the optimal pyrolysis temperature was explored. Ni@NCNs were systematically characterized by wide analytical techniques. In the hydrogenation of p-chloronitrobenzene, Ni@NCNs-600 (pyrolyzed at 600 °C) exhibited extraordinarily high performance with 77.9 h–1 catalytic productivity and > 99% p-chloroaniline selectivity at full p-chloronitrobenzene conversion under mild conditions (90 °C, 1.5 MPa H2), showing obvious superiority compared with reported Ni-based catalysts. Notably, the reaction smoothly proceeded at room temperature with full conversion and > 99% selectivity. Moreover, Ni@NCNs-600 afforded good tolerance to various nitroarenes substituted by sensitive groups (halogen, nitrile, keto, carboxylic, etc.), and could be easily recycled by magnetic separation and reused for 5 times without deactivation. The adsorption tests showed that the preferential adsorption of –NO2 on the catalyst can restrain the dehalogenation of p-chloronitrobenzene, thus achieving high p-chloroaniline selectivity. While the high activity can be attributed to high Ni dispersion, special morphology, and rich pore structure of the catalyst.