Abstract:A series of N-doped carbon materials (NCs) were synthesized by using biomass citric acid and dicyandiamide as renewable raw materials via a facile one-step pyrolysis method. The characterization of microstructural features shows that the NCs samples are composed of few-layered graphene-like nanoflakes with controlled in situ N doping, which is attributed to the confined pyrolysis of citric acid within the interlayers of the dicyandiamide-derived g-C3N4 with high nitrogen contents. Evidently, the pore volumes of the NCs increased with the increasing content of dicyandiamide in the precursor. Among these samples, the NCs nanoflakes prepared with the citric acid/dicyandiamide mass ratio of 1:6, NC-6, show the highest N content of ~6.2 at%, in which pyridinic and graphitic N groups are predominant. Compared to the commercial Pt/C catalyst, the as-prepared NC-6 exhibits a small negative shift of ~66 mV at the half-wave potential, demonstrating excellent electrocatalytic activity in the oxygen reduction reaction. Moreover, NC-6 also shows better long-term stability and resistance to methanol crossover compared to Pt/C. The efficient and stable performance are attributed to the graphene-like microstructure and high content of pyridinic and graphitic doped nitrogen in the sample, which creates more active sites as well as facilitating charge transfer due to the close four-electron reaction pathway. The superior electrocatalytic activity coupled with the facile synthetic method presents a new pathway to cost-effective electrocatalysts for practical fuel cells or metal-air batteries.

Templated Synthesis of Exfoliated Porous Carbon with Dominant Graphitic Nitrogen

Facile synthesis of porous carbon materials with extra high nitrogen content for supercapacitor electrodes

All-solid-state synthesis of nitrogen doped carbon with high-faradaic-active species for supercapacitor

A template-catalyzed in situ polymerization and co-assembly strategy for rich nitrogen-doped mesoporous carbon

Synthesis of Sandwich-Like Graphene@mesoporous Nitrogen-Doped Carbon Nanosheets for Application in High-Performance Supercapacitors

Nitrogen‐Doped Nanoporous Graphenic Carbon: An Efficient Conducting Support for O

Facile synthesis of nitrogen-enriched nanoporous carbon materials for high performance supercapacitors.

A controllable synthesis of rich nitrogen-doped ordered mesoporous carbon for CO2 capture and supercapacitors

Direct synthesis of nitrogen-doped carbon nanosheets with high surface area and excellent oxygen reduction performance

Molecular Engineering toward High‐Crystallinity Yet High‐Surface‐Area Porous Carbon Nanosheets for Enhanced Electrocatalytic Oxygen Reduction

Facile synthesis of microporous N-doped carbon material and its application in supercapacitor

Facile Synthesis of N-Doped Graphene-Like Carbon Nanoflakes as Efficient and Stable Electrocatalysts for the Oxygen Reduction Reaction

Graphene-Directed Formation of a Nitrogen-Doped Porous Carbon Sheet with High Catalytic Performance for the Oxygen Reduction Reaction

Templated transformation of g-C3N4 nanosheets into nitrogen-doped hollow carbon sphere with tunable nitrogen-doping properties for application in Li-ions batteries

Coal Tar Pitch Derived N-doped Porous Carbon Nanosheets by the In-Situ Formed G-C3n4 As a Template for Supercapacitor Electrodes

N-doped Hierarchically Micro- and Mesoporous Carbons with Superior Performance in Supercapacitors

Impregnation Assisted Synthesis of 3d Nitrogen-Doped Porous Carbon with High Capacitance

Nitrogen-doped Hierarchically Ellipsoidal Porous Carbon Derived from Al-based Metal-Organic Framework with Enhanced Specific Capacitance and Rate Capability for High Performance Supercapacitors

Nitrogen-Doped Hierarchical Porous Carbon Nanowhisker Ensembles on Carbon Nanofiber for High-Performance Supercapacitors

A Simple Synthesis of an N-Doped Carbon ORR Catalyst: Hierarchical Micro/Meso/Macro Porosity and Graphitic Shells

One-Step Synthesis of Microporous Carbon Monoliths Derived from Biomass with High Nitrogen Doping Content for Highly Selective CO2 Capture.