Abstract:The red mud-based ZIF-67 composite (ZIF-67/RM) was synthesized by a simple coprecipitation method and employed as a heterogeneous catalyst for activating peroxymonosulfate (PMS) to degrade ciprofloxacin (CIP). The optimum preparation conditions of ZIF-67 were as follows: Co(NO3)(2)6H(2)O dosage 10 mmol, 2-MeIM dosage 80 mmol, RM dosage 3 g, stirring time 3 h, stirring temperature 60 degrees C, stirring speed 640 rpm. Under the conditions of ZIF-67/RM dosage 0.1 g/L, PMS concentration 0.2 mM, CIP concentration 20 mg/L, and pH = 7, the maximal removal rate of CIP could reach about 82.4 % at the reaction time of 30 min. The SEM and BET characterization results showed that the rhombohedral dodecahedral ZIF-67 could fully fill the large pores of RM and form additional pore structures on the surface of RM due to its small particle size and regular shape. This phenomenon was conducive to the increase of specific surface area and the provision of more active sites for ZIF-67/RM composites. The comparative experiments revealed that Fe in RM and Co in ZIF-67 exhibited a positive synergistic catalytic effect for CIP removal. Quenching experiment, electron paramagnetic resonance (EPR) and high performance liquid chromatography (HPLC) analysis showed that Fe(IV) and Co(IV) played a leading role in the ZIF-67/RM/PMS system. At the same time, a large number of reactive oxygen species (ROS) were also produced to participate in the oxidative degradation process. The chronoamperometry experiment showed that electron transfer had little effect on CIP degradation. Furthermore, the catalytic mechanism of the PMS activated by ZIF-67/RM was proposed. DFT calculations and LC-MS analysis deduced the degradation pathway of CIP. Using the principles of quantitative structure-activity relationship (QSAR), the ecotoxicity of the degradation intermediates was analyzed. The recycling experiment, FT-IR, and XRD demonstrated that the presence of Fe-O-Co bonds prevented the leaching of Co and Fe ions, thus ZIF-67/RM exhibiting good stability. In this work, novel insights are provided into the design of composite materials based on RM and metal-organic frameworks (MOFs) as heterogeneous catalysts for the effective treatment of antibiotic wastewater through PMS activation.

Highly efficient activation of peroxymonosulfate by ZIF-67 anchored cotton derived for ciprofloxacin degradation

Degradation of Ciprofloxacin Using Α-Mno2 Activated Peroxymonosulfate Process: Effect of Water Constituents, Degradation Intermediates and Toxicity Evaluation

Zinc-based metal–organic framework nanofibers membrane ZIF-65/PAN as efficient peroxymonosulfate activator to degrade aqueous ciprofloxacin

Efficient Degradation of Ciprofloxacin by Peroxymonosulfate Activated Using Red Mud-Based ZIF-67 Composite As a Heterogeneous Catalyst

Photo-assisted peroxymonosulfate activation with the heterostructure of ZIF-67@MIL-100(Fe) for ciprofloxacin degradation: Reactivity, stability, and synergistic mechanisms

ZSM-5-(C@Fe) activated peroxymonosulfate for effectively degrading ciprofloxacin: In-depth analysis of degradation mode and degradation path

Enhanced peroxymonosulfate activation for rapid degradation of ciprofloxacin using a novel ternary ZIF-67@MnOOH@GO composite

Highly efficient activation of peroxymonosulfate by MOF derived CoS2@C for degradation of ciprofloxacin

Activation of peroxymonosulfate for ciprofloxacin degradation by a novel oxygen-deficient CoTiO 3 /TiO 2 NTs/Ti composite catalytic membrane:Electron transfer pathway and underlying mechanism

Mn3O4-ZnMn2O4/SnO2 Nanocomposite Activated Peroxymonosulfate for Efficient Degradation of Ciprofloxacin in Water

Highly Efficient Activation of Peroxymonosulfate by Cobalt Sulfide Hollow Nanospheres for Fast Ciprofloxacin Degradation

Efficient removal of oxytetracycline hydrochloride by ZIF-67 coated hollow spherical CuS (CuS-PVP@ZIF-67) under the synergistic effect of adsorption and PMS activation

Electron transfer mechanism mediated MOF-derived nanoflowers catalyst for promoting peroxymonosulfate activation and ciprofloxacin degradation

Highly Efficient Peroxymonosulfate Activation by MOFs-derived Oxygen Vacancy-Rich Co3O4/ZnO P-N Heterojunction Nanocomposites to Degrade Pefloxacin

Efficient peroxymonosulfate activation by MOFs derived cobalt-carbon composite for nonradical degradation of ciprofloxacin via Co(IV) = O

Highly efficient targeted adsorption and catalytic degradation of ciprofloxacin by a novel molecularly imprinted bimetallic MOFs catalyst for persulfate activation

Efficient Degradation of Ciprofloxacin by 3D Oxygen-Doped MoS2/polyacrylamide/graphene Oxide Composite Hydrogel Co-Catalytic Fenton Reaction

Tetracycline degradation by activated persulfate with enhancement of ZIF-67 loaded wood-microreactor

MOFs meet wood with enlarged pores: A high-capacity and efficient removal of ciprofloxacin from water

MOF-derived FeCo carbon nanomaterials with abundant oxygen vacancies as highly efficient peroxymonosulfate catalyst for ciprofloxacin degradation

Copper substituted zinc ferrite with abundant oxygen vacancies for enhanced ciprofloxacin degradation via peroxymonosulfate activation.