Cobalt-Nanoparticle-Decorated Cobalt–Molybdenum Bimetal Oxides Embedded in Flower-like N-Doped Carbon as a Durable and Efficient Electrocatalyst for Oxygen Evolution Reaction
Yanan Zhang,Wenlong Ye,Jinchen Fan,Volkan Cecen,Penghui Shi,Yulin Min,Qunjie Xu
DOI: https://doi.org/10.1021/acssuschemeng.1c02472
2021-08-09
Abstract:The development of high-efficiency and cost-efficient oxygen evolution reaction (OER) catalysts is a core issue in the sector of water electrolysis. Cobalt–molybdenum bimetal oxide (Co2Mo3O8), as a kind of non-noble transition-metal oxides, is broadly employed as a good OER catalyst due to its abundant active sites. However, the relatively low conductivity of Co2Mo3O8 limits further improvement in its electrocatalytic performance. Herein, the cobalt nanoparticle-modified Co2Mo3O8 flakes are embedded into the flower-like N-doped carbon (NC) microspheres to effectively improve the electrocatalytic OER performance. The combination of Co2Mo3O8 and NC with a flower-like structure effectively improves the conductivity of the material while enhancing the electrolyte penetration. More importantly, the Co nanoparticles (NPs) on the surface of Co2Mo3O8 flakes have the capability to furnish more active electrocatalytic active sites. The obtained Co NP-modified Co2Mo3O8 embedded flower-like NC microspheres (Co/Co2Mo3O8@NC) exhibited an overpotential of 288 mV at 10 mA·cm–2, which was relatively low in comparison to that of commercial RuO2. Besides, the Co/Co2Mo3O8@NC also shows long-term durability almost without attenuation after the 44 000 s I–T test.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.1c02472.Detailed information of the preparation processes of , Co3O4@NC, and MoO3 nanorods, XRD pattern of CoMo-MOFs, Co 2p and Mo 3d core-level XPS spectra of Co/Co2Mo3O8@NC and Co2Mo3O8@NC, N2 adsorption–desorption isotherms of Co/Co2Mo3O8@NC, pore size distributions of Co/Co2Mo3O8@NC, equivalent circuit model used for simulating the Nyquist plots, electrochemical capacitance measurements for Co/Co2Mo3O8@NC, , Co3O4@NC MoO3, and Co2Mo3O8@NC, comparison of the OER performance of Co/Co2Mo3O8@NC with those of the recently reported Co- or Mo-based electrocatalysts; and SEM images of Co/Co2Mo3O8@NC catalyst (a) before and (b) after I–T test of 44 000 s (PDF)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology