What's new in sports medicine.

Mark D. Miller

DOI: https://doi.org/10.2106/00004623-200403000-00041

Abstract:

What problem does this paper attempt to address?

3D Printing of Biomimetic Multi-Layered GelMA/nHA Scaffold for Osteochondral Defect Repair

Jingyi Liu,Liang Li,Hairui Suo,Mengling Yan,Jun Yin,Jianzhong Fu

DOI: https://doi.org/10.1016/j.matdes.2019.107708

IF: 9.417

2019-01-01

Materials & Design

Abstract:Currently, osteochondral defects frequently cause limited motion and impaired function of the joint, leading to serious healthcare problems, and it is still very challenging to realize the simultaneous regeneration of subchondral bone with cartilage. In the current study, we designed a tri-layered scaffold and fabricated it using the extrusion-based multi-nozzle 3D printing technology. The bioinks used for 3D printing included a 15% methacrylated gelatin (GelMA) hydrogel for cartilage on top layer, a combination of 20% GelMA and 3% nanohydroxyapatite (nHA) (20/3% GelMA/nHA) hydrogel for interfacial layer, and a 30/3% GelMA/nHA hydrogel for subchondral bone at bottom layer. The water absorption capacity, biodegradation, and mechanical properties of hydrogels and scaffolds were characterized, and in vitro assay with bone marrow mesenchymal stem cells (BMSCs) was performed to indicate the biocompatibility of scaffolds. Based on the results of in vivo repair of rabbit osteochondral defect, the neo-tissues in defects integrated better with the surrounding tissues, the joint surface of the defects was smoother, and more cartilage-specific extracellular matrix and collagen type II were observed using the tri-layered scaffolds. This study not only provides a potential manufacturing method for multi-layered scaffolds, but also is helpful for understanding the regeneration mechanism of cartilage-subchondral bone.
3D bioprinting by reinforced bioink based on photocurable interpenetrating networks for cartilage tissue engineering

Jingjie Shen,Wenjing Song,Jia Liu,Xiaoyun Peng,Zhuhao Tan,Yingni Xu,Sa Liu,Li Ren

DOI: https://doi.org/10.1016/j.ijbiomac.2023.127671

IF: 8.2

2023-11-06

International Journal of Biological Macromolecules

Abstract:Cartilage has a limited ability to repair itself, highlighting the urgent need for suitable materials for cartilage regeneration. Achieving a balance between cell survival environment and hydrogel crosslinking density is crucial for photosensitive cell-laden cartilage repair materials to achieve both high strength and good cell viability. Here, an interpenetrating hydrogel consisted of methacrylate gelatin (GelMA) and glycidyl methacrylate silk fibroin (SG) was introduced. Compared to GelMA hydrogel, GelMA/SG had desired mechanical properties, with achieving up to 5 times of compression modulus and 6 times of compression failure energy. Meanwhile, the chondrocytes inside GelMA/SG exhibited great viability which was over 90 %. GelMA/SG as a bioink had favorable printability for digital light processing (DLP) bioprinting. The mesh DLP-printed scaffolds with high precision were created and GelMA/SG had a better shape retention ability than GelMA. Moreover, GelMA/SG cell-laden scaffolds had high strength while chondrocytes proliferated significantly in vitro culture. They were implanted under the skin of nude mice to evaluate ectopic chondrogenesis in vivo . The GelMA/SG cell-laden scaffolds indicated little deformation and high expression of collagen type II and glycosaminoglycans, which was advantageous for cartilage regeneration. The scaffold and its fabrication strategy provide potential solutions for clinical cartilage repair problems in the future.

polymer science,biochemistry & molecular biology,chemistry, applied
Daily management systems in medicine.

L. Donnelly

DOI: https://doi.org/10.1148/rg.342130035

2014-03-01

Radiographics

Abstract:"Lean" (continuous improvement) organizations make use of daily management systems (DMS) that are designed so that problems can be quickly identified, front-line staff are empowered to fix the problems that they can, and problems that the front-line staff cannot fix are escalated and countermeasures created quickly. Key components of a DMS include leadership standard work, visual controls, and a daily accountability process, as well as discipline involving each of these three components. The author's organization recently had the opportunity to open a new, nonreplacement hospital, allowing the incorporation of continuous improvement principles into the hospital's design and operations. One high-priority task was the creation of a DMS, which was structured as a tiered "huddle" system. All of the front-line clinical areas, as well as all clinical and nonclinical ancillary support areas, conduct morning huddles. Problems identified at these huddles and needing escalation are then brought to a patient flow huddle and an integrated huddle. All of these huddles occur daily and have a standard format with three clearly defined components: metrics-goal review, daily readiness assessment, and problem accountability reporting. The huddles also provide a daily opportunity to see and converse with the people with whom one needs to discuss certain issues. The process of bringing people together for these huddles can contribute significantly to team formation, coordination of efforts, and development of a culture of trust.
Fabrication of 3D-Printed Interpenetrating Hydrogel Scaffolds for Promoting Chondrogenic Differentiation

Jian Guan,Fu-zhen Yuan,Zi-mu Mao,Hai-lin Zhu,Lin Lin,Harry Huimin Chen,Jia-kuo Yu

DOI: https://doi.org/10.3390/polym13132146

IF: 5

2021-06-29

Polymers

Abstract:The limited self-healing ability of cartilage necessitates the application of alternative tissue engineering strategies for repairing the damaged tissue and restoring its normal function. Compared to conventional tissue engineering strategies, three-dimensional (3D) printing offers a greater potential for developing tissue-engineered scaffolds. Herein, we prepared a novel photocrosslinked printable cartilage ink comprising of polyethylene glycol diacrylate (PEGDA), gelatin methacryloyl (GelMA), and chondroitin sulfate methacrylate (CSMA). The PEGDA-GelMA-CSMA scaffolds possessed favorable compressive elastic modulus and degradation rate. In vitro experiments showed good adhesion, proliferation, and F-actin and chondrogenic differentiation of bone marrow mesenchymal stem cells (BMSCs) on the scaffolds. When the CSMA concentration was increased, the compressive elastic modulus, GAG production, and expression of F-actin and cartilage-specific genes (COL2, ACAN, SOX9, PRG4) were significantly improved while the osteogenic marker genes of COL1 and ALP were decreased. The findings of the study indicate that the 3D-printed PEGDA-GelMA-CSMA scaffolds possessed not only adequate mechanical strength but also maintained a suitable 3D microenvironment for differentiation, proliferation, and extracellular matrix production of BMSCs, which suggested this customizable 3D-printed PEGDA-GelMA-CSMA scaffold may have great potential for cartilage repair and regeneration in vivo.

polymer science
Structurally and Functionally Optimized Silk-Fibroin-Gelatin Scaffold Using 3D Printing to Repair Cartilage Injury In Vitro and In Vivo.

Weili Shi,Muyang Sun,Xiaoqing Hu,Bo Ren,Jin Cheng,Chenxi Li,Xiaoning Duan,Xin Fu,Jiying Zhang,Haifeng Chen,Yingfang Ao

DOI: https://doi.org/10.1002/adma.201701089

IF: 29.4

2017-01-01

Advanced Materials

Abstract:Articular cartilage repair remains a great challenge for clinicians and researchers. Recently, there emerges a promising way to achieve one-step cartilage repair in situ by combining endogenic bone marrow stem cells (BMSCs) with suitable biomaterials using a tissue engineering technique. To meet the increasing demand for cartilage tissue engineering, a structurally and functionally optimized scaffold is designed, by integrating silk fibroin with gelatin in combination with BMSC-specific-affinity peptide using 3D printing (3DP) technology. The combination ratio of silk fibroin and gelatin greatly balances the mechanical properties and degradation rate to match the newly formed cartilage. This dually optimized scaffold has shown superior performance for cartilage repair in a knee joint because it not only retains adequate BMSCs, due to efficient recruiting ability, and acts as a physical barrier for blood clots, but also provides a mechanical protection before neocartilage formation and a suitable 3D microenvironment for BMSC proliferation, differentiation, and extracellular matrix production. It appears to be a promising biomaterial for knee cartilage repair and is worthy of further investigation in large animal studies and preclinical applications. Beyond knee cartilage, this dually optimized scaffold may also serve as an ideal biomaterial for the regeneration of other joint cartilages.
3D Printing of Microenvironment‐Specific Bioinspired and Exosome‐Reinforced Hydrogel Scaffolds for Efficient Cartilage and Subchondral Bone Regeneration

Qi Li,Huilei Yu,Fengyuan Zhao,Chenxi Cao,Tong Wu,Yifei Fan,Yingfang Ao,Xiaoqing Hu

DOI: https://doi.org/10.1002/advs.202303650

IF: 15.1

2023-07-10

Advanced Science

Abstract:A novel tissue‐specific microenvironment biomimetic and exosome‐reinforced hydrogel scaffold for complex heterogeneous tissue regeneration is designed. The 3D‐printed bioinspired hydrogel scaffold can efficiently promote mesenchymal stem cell lineage‐specific differentiation and osteochondral regeneration in a rat model. The strategy provides a promising platform for physiological regeneration of complex zonal tissue and holds attractive clinical translation potential. In clinical practice, repairing osteochondral defects presents a challenge due to the varying biological properties of articular cartilages and subchondral bones. Thus, elucidating how spatial microenvironment‐specific biomimetic scaffolds can be used to simultaneously regenerate osteochondral tissue is an important research topic. Herein, a novel bioinspired double‐network hydrogel scaffold produced via 3D printing with tissue‐specific decellularized extracellular matrix (dECM) and human adipose mesenchymal stem cell (MSC)‐derived exosomes is described. The bionic hydrogel scaffolds promote rat bone marrow MSC attachment, spread, migration, proliferation, and chondrogenic and osteogenic differentiation in vitro, as determined based on the sustained release of bioactive exosomes. Furthermore, the 3D‐printed microenvironment‐specific heterogeneous bilayer scaffolds efficiently accelerate the simultaneous regeneration of cartilage and subchondral bone tissues in a rat preclinical model. In conclusion, 3D dECM‐based microenvironment‐specific biomimetics encapsulated with bioactive exosomes can serve as a novel cell‐free recipe for stem cell therapy when treating injured or degenerative joints. This strategy provides a promising platform for complex zonal tissue regeneration whilst holding attractive clinical translation potential.

materials science, multidisciplinary,nanoscience & nanotechnology,chemistry
ECM-Mimicking Hydrogels Loaded with Bone Mesenchymal Stem Cell-Derived Exosomes for the Treatment of Cartilage Defects

Jiyun Cheng,Genxiang Rong,Ziqi Wang,Shencai Liu,Qinfeng Yang,Weilu Liu,Dongkun Zhang,Jianwei Li

DOI: https://doi.org/10.1155/2022/3450672

2022-11-03

Abstract:It is well-established that treating articular cartilage injuries is clinically challenging since they lack blood arteries, nerves, and lymphoid tissue. Recent studies have revealed that bone marrow stem cell-derived exosomes (BMSCs-Exos) exert significant chondroprotective effects through paracrine secretions, and hydrogel-based materials can synergize the exosomes through sustained release. Therefore, this research aims to synthesize an ECM (extracellular matrix)-mimicking gelatin methacryloyl (GelMA) hydrogel modified by gelatin combined with BMSCs-derived exosomes to repair cartilage damage. We first isolated and characterized exosomes from BMSCs supernatant and then loaded the exosomes into GelMA hydrogel to investigate cartilage repair effects in in vitro and in vivo experiments. The outcomes showed that the GelMA hydrogel has good biocompatibility with a 3D (three-dimensional) porous structure, exhibiting good carrier characteristics for exosomes. Furthermore, BMSCs-Exos had a significant effect on promoting chondrocyte ECM production and chondrocyte proliferation, and the GelMA hydrogel could enhance this effect through a sustained-release effect. Similarly, in vivo experiments showed that GelMA-Exos promoted cartilage regeneration in rat joint defects and the synthesis of related cartilage matrix proteins.
Experimental study on repair of cartilage defects in the rabbits with GelMA-MSCs scaffold prepared by three-dimensional bioprinting

Zijie Pei,Mingyang Gao,Junhui Xing,Changbao Wang,Piqian Zhao,Hongtao Zhang,Jing Qu

DOI: https://doi.org/10.18063/ijb.v9i2.662

2023-01-05

International Journal of Bioprinting

Abstract:Cartilage damage is a common orthopedic disease, which can be caused by sports injury, obesity, joint wear, and aging, and cannot be repaired by itself. Surgical autologous osteochondral grafting is often required in deep osteochondral lesions to avoid the later progression of osteoarthritis. In this study, we fabricated a gelatin methacryloyl-marrow mesenchymal stem cells (GelMA-MSCs) scaffold by three-dimensional (3D) bioprinting. This bioink is capable of fast gel photocuring and spontaneous covalent cross-linking, which can maintain high viability of MSCs and provide a benign microenvironment to promote the interaction, migration, and proliferation of cells. In vivo experiments, further, proved that the 3D bioprinting scaffold can promote the regeneration of cartilage collagen fibers and have a remarkable effect on cartilage repair of rabbit cartilage injury model, which may represent a general and versatile strategy for precise engineering of cartilage regeneration system.

engineering, biomedical,materials science, biomaterials
Bioprinted Biomimetic Hydrogel Matrices Guiding Stem Cell Aggregates for Enhanced Chondrogenesis and Cartilage Regeneration

Yuetian Liu,Lijuan Du,Hua Zhang,Guanrong Li,Yang Luo,Zeming Hu,Rong Xu,Jie Yao,Zheyuan Shi,Yige Chen,Chi Zhang,Zhanping Jin,Caihua Zhang,Chanchan Xie,Jun Fu,Yabin Zhu,Yingchun Zhu

DOI: https://doi.org/10.1039/d4tb00323c

IF: 7.571

2024-04-24

Journal of Materials Chemistry B

Abstract:Articular cartilage tissue has limited self-repair capability, with damage frequently progressing to irreversible degeneration. Engineered tissues constructed through bioprinting and embedded with stem cell aggregates offer promising therapeutic alternatives. Aggregates of bone marrow mesenchymal stromal cells (BMSCs) demonstrate enhanced and more rapid chondrogenic differentiation than isolated cells, thus facilitating cartilage repair. However, it remains a key challenge to precisely control biochemical microenvironments to regulate cellular adhesion and cohesion within bioprinted matrices simultaneously. Herein, this work reports a bioprintable hydrogel matrix with high cellular adhesion and aggregation properties for cartilage repair. The hydrogel comprises an enhanced cell-adhesive gelatin methacrylate and a cell-cohesive chitosan methacrylate (CHMA), both of which are subjected to photo-initiated crosslinking. By precisely adjusting the CHMA content, the mechanical stability and biochemical cues of the hydrogels are finely tuned to promote cellular aggregation, chondrogenic differentiation and cartilage repair implantation. Multi-layer constructs encapsulated with BMSCs, with high viability above 91.1%, are bioprinted and photo-crosslinked to support chondrogenic differentiation for 21 days. BMSCs rapidly form aggregates and display efficient chondrogenic differentiation both on the hydrogels and within bioprinted constructs, as evidenced by the upregulated expression of Sox9, Aggrecan and Collagen 2a1 genes, along with high protein levels. Transplantation of these BMSC-laden bioprinted hydrogels into cartilaginous defects demonstrates effective hyaline cartilage repair. Overall, this cell-responsive hydrogel scaffold holds immense promise for applications in cartilage tissue engineering.

materials science, biomaterials
Cell‐Free Bilayered Porous Scaffolds for Osteochondral Regeneration Fabricated by Continuous 3D‐Printing Using Nascent Physical Hydrogel as Ink

Jingming Gao,Xiaoquan Ding,Xiaoye Yu,Xiaobin Chen,Xingyu Zhang,Shuquan Cui,Jiayue Shi,Jun Chen,Lin Yu,Shiyi Chen,Jiandong Ding

DOI: https://doi.org/10.1002/adhm.202001404

IF: 10

2020-11-23

Advanced Healthcare Materials

Abstract:<p>Cartilage is difficult to self‐repair and it is more challenging to repair an osteochondral defects concerning both cartilage and subchondral bone. Herein, it is hypothesized that a bilayered porous scaffold composed of a biomimetic gelatin hydrogel may, despite no external seeding cells, induce osteochondral regeneration in vivo after being implanted into mammal joints. This idea is confirmed based on the successful continuous 3D‐printing of the bilayered scaffolds combined with the sol‐gel transition of the aqueous solution of a gelatin derivative (physical gelation) and photocrosslinking of the gelatin methacryloyl (gelMA) macromonomers (chemical gelation). At the direct printing step, a nascent physical hydrogel is extruded, taking advantage of non‐Newtonian and thermoresponsive rheological properties of this 3D‐printing ink. In particular, a series of crosslinked gelMA (GelMA) and GelMA‐hydroxyapatite bilayered hydrogel scaffolds are fabricated to evaluate the influence of the spacing of 3D‐printed filaments on osteochondral regeneration in a rabbit model. The moderately spaced scaffolds output excellent regeneration of cartilage with cartilaginous lacunae and formation of subchondral bone. Thus, tricky rheological behaviors of soft matter can be employed to improve 3D‐printing, and the bilayered hybrid scaffold resulting from the continuous 3D‐printing is promising as a biomaterial to regenerate articular cartilage.</p>

nanoscience & nanotechnology,engineering, biomedical,materials science, biomaterials
3D printing viscoelastic hydrogel-based scaffolds with a swelling-dependent gate for cartilage injury regeneration

Anan Zhang,Lili Sun,Kai Chen,Changsheng Liu,Yuan Yuan

DOI: https://doi.org/10.1016/j.cej.2023.147260

IF: 15.1

2023-12-16

Chemical Engineering Journal

Abstract:Regeneration of articular cartilage remains a great challenge due to its poor self-healing capacity and weak stability. The microfracture surgery (MF) can provide bone marrow mesenchymal stem cells (BMSCs) and is commonly used in clinical practice, but its therapeutic effect is still limited by the lack of effective adhesion matrix and the uncontrollable tendency to develop fibrosis and even mineralization. In this study, a small molecular drug-loaded viscoelastic hydrogel-based 3D printing bilayer scaffold with a swelling-dependent gate was successfully developed to address these limitations. The scaffold consisted of a lower layer with a smaller pore size and an upper matrix with larger pore size. The former acted as a swelling-dependent gate to switch pore size, which initially was on-state allowing the infiltration of BMSCs, and eventually transformed into off-state serving as a barrier blocking excessive blood support from the bone marrow after swelling-induced closure of pores. This barrier structure cooperated with fatty acid inhibitor-suppressed hypertrophy of neo-cartilage matrix. The latter provided a biocompatible and viscoelastic matrix to guide MSCs toward stable chondrogenic commitment. By integrating structural design with the inhibitor, the bilayer scaffold provides a promising platform for future clinical applications of MF surgery in cartilage regeneration.

engineering, chemical, environmental
Low temperature 3D printing of tissue cartilage engineered with gelatin methacrylamide.

Chunyang Luo,Rui Xie,Jiyong Zhang,Yang Liu,Zuxi Li,Yi Zhang,Xiao Zhang,Tao Yuan,Yinan Chen,Weimin Fan

DOI: https://doi.org/10.1089/ten.TEC.2020.0053

2020-01-01

Abstract:Low concentration Gelatin methacryloyl (GelMA) hydrogels have been found to be promising cell-laden bioinks with excellent cell viability. Herein, we report a strategy that accurately deposits cell-containing bioinks at 5％ (w/v) GelMA using extrusion 3D bioprinting technology by utilizing its photo-crosslinkable and thermosensitive properties without the need for any sacrificial materials. During the 3D printing process, regular, smooth microfibers were formed without any discontinuity of extrusion or clogging, and photo-crosslinking was then used to stabilize the printed GelMA structure. After printing, the scaffolds were cultured in a chondrogenic medium to evaluate their significant roles in directing the behaviors of bone mesenchymal stem cells (BMSCs). Evidence of chondrogenic differentiation was demonstrated by Alcian blue staining and immunofluorescence (Col2a1) as well as the expression of chondrogenic genes. Finally, after platelet-rich plasma (PRP) treatment, the in vivo effects of the BMSCs on cartilage regeneration on the thigh muscles of female nude mice were measured using immunohistochemical techniques. The results showed that with this strategy, GelMA bioink displays excellent printability and a high cell survival rate. In vitro and in vivo, the cell-laden scaffold successfully regenerated mature cartilage via a cartilage-specific extracellular matrix, which seems to be suitable for cartilage regeneration and repair.
Low-Temperature Three-Dimensional Printing of Tissue Cartilage Engineered With Gelatin Methacrylamide

Chunyang Luo,Rui Xie,Jiyong Zhang,Yang Liu,Zuxi Li,Yi Zhang,Xiao Zhang,Tao Yuan,Yinan Chen,Weimin Fan

DOI: https://doi.org/10.1089/ten.tec.2020.0053

2020-01-01

Abstract:Impact statement Gelatin methacryloyl is a promising material in tissue engineering and has been widely studied in three-dimensional bioprinting. In this study, we report a strategy for precise deposition of a cell-laden gelatin methacrylamide bioink at low concentration by using three-dimensional bioprinting. Cell-laden 5% (w/v) gelatin methacrylamide was successfully printed without any construct deformation or collapse and was permanently crosslinked by blue light. The results indicate that with this strategy, 5% (w/v) gelatin methacrylamide bioink exhibited excellent printability and printing resolution with high cell viability. Bone mesenchymal stem cells could be differentiated into chondrocytes when they were cultured with 5% GelMAin vitroand formed cartilage-like tissues after intramuscular implantation when the constructs were treated with platelet-rich plasma. Low-concentration gelatin methacryloyl (GelMA) hydrogels have been found to be promising cell-laden bioinks with excellent cell viability. Herein, we report a strategy that accurately deposits cell-containing bioinks at 5% (w/v) GelMA using extrusion three-dimensional (3D) bioprinting technology by utilizing its photo-crosslinkable and thermosensitive properties without the need for any sacrificial materials. During the 3D printing process, regular, smooth microfibers were formed without any discontinuity of extrusion or clogging, and photo-crosslinking was then used to stabilize the printed GelMA structure. After printing, the scaffolds were cultured in a chondrogenic medium to evaluate their significant roles in directing the behaviors of bone mesenchymal stem cells (BMSCs). Evidence of chondrogenic differentiation was demonstrated by Alcian blue staining and immunofluorescence (Col2a1) as well as the expression of chondrogenic genes. Finally, after platelet-rich plasma treatment, thein vivoeffects of the BMSCs on cartilage regeneration on the thigh muscles of female nude mice were measured by using immunohistochemical techniques. The results showed that with this strategy, GelMA bioink displays excellent printability and a high cell survival rate.In vitroandin vivo, the cell-laden scaffold successfully regenerated mature cartilage via a cartilage-specific extracellular matrix, which seems to be suitable for cartilage regeneration and repair.
A Gelatin-Hyaluronic Acid Double Cross-Linked Hydrogel for Regulating the Growth and Dual Dimensional Cartilage Differentiation of Bone Marrow Mesenchymal Stem Cells.

Lingrong Liu,Han Zhang,Qiqing Zhang,Ying Ren,Yuan Zhang,Yunping Wang

DOI: https://doi.org/10.1166/jbn.2021.3088

2021-06-01

Journal of Biomedical Nanotechnology

Abstract:Owing to its unique physiochemical properties similar to the extracellular matrix (ECM), three-dimensional (3D) crosslinked hydrogels are widely studied materials for tissue engineering. In this study, to mimic the ECM microenvironment, a two-step covalent cross-linking with hyaluronic acid and gelatin was performed to form an interpenetrating polymer network structure. Gelatin as the first network greatly improved the mechanical strength of the hydrogels, while a hyaluronic acid network as the second network improved the tenacity and biological activity. Compared with a single network hydrogel, the interpenetrating hydrogel system can further regulate the mechanical properties of the hydrogel by adjusting the ratio of the two components, thereby changing the proliferation, activity, and direction of cartilage differentiation of bone marrow mesenchymal stem cells (BMSCs). Not only that, with two culture methods for BMSCs on the surface and 3D wrapped in the double cross-linked hydrogels, they exhibited their potential to induce BMSCs to cartilage differentiation under the condition of 3D encapsulation of BMSCs and contact with BMSCs on its surface. As a scaffold material for cartilage tissue engineering, this double cross-linked hydrogel demonstrated its high feasibility and applicability in delivering BMSCs in vivo and repairing defects.

Engineering,Medicine,Materials Science
3D Bioprinting of Bone Marrow Mesenchymal Stem Cell-Laden Silk Fibroin Double Network Scaffolds for Cartilage Tissue Repair

Tianyu Ni,Min Liu,Yajie Zhang,Yi Cao,Renjun Pei

DOI: https://doi.org/10.1021/acs.bioconjchem.0c00298

IF: 4.7

2020-01-01

Bioconjugate Chemistry

Abstract:3D bioprinting is one of the latest trends in regenerative medicine due to its capacity for constructing highly organized tissues with living cells. In this work, silk fibroin (SF) together with hydroxypropyl methyl cellulose (HPMC) was used to print bone marrow mesenchymal stem cell (BMSC)-laden double network (DN) hydrogel for cartilage tissue repair. The β-sheet structure formed among SF molecules was set as the rigid and brittle first network, while the cross-linking of HPMC-MA was set as the soft and ductile second network. Compared to the single network hydrogel, the fracture strength, breaking elongation, and compressive reproducibility increased significantly. Thereafter, the evaluation of cell proliferation and biochemical assay of this BMSC-laden 3D bioprinted hydrogel proved that it could ensure sufficient nutrient supply and great biochemical supportability in tissue engineering. This SF-based bioink with remarkable mechanical properties holds great promise as candidate for cartilage tissue regeneration.
3D Bioprinting of Biomimetic Bilayered Scaffold Consisting of Decellularized Extracellular Matrix and Silk Fibroin for Osteochondral Repair

Xiao Zhang,Yang Liu,Qiang Zuo,Qingyun Wang,Zuxi Li,Kai Yan,Tao Yuan,Yi Zhang,Kai Shen,Rui Xie,Weimin Fan

DOI: https://doi.org/10.18063/ijb.v7i4.401

International Journal of Bioprinting

Abstract:Recently, three-dimensional (3D) bioprinting technology is becoming an appealing approach for osteochondral repair. However, it is challenging to develop a bilayered scaffold with anisotropic structural properties to mimic a native osteochondral tissue. Herein, we developed a bioink consisting of decellularized extracellular matrix and silk fibroin to print the bilayered scaffold. The bilayered scaffold mimics the natural osteochondral tissue by controlling the composition, mechanical properties, and growth factor release in each layer of the scaffold. The in vitro results show that each layer of scaffolds had a suitable mechanical strength and degradation rate. Furthermore, the scaffolds encapsulating transforming growth factor-beta (TGF-β) and bone morphogenetic protein-2 (BMP-2) can act as a controlled release system and promote directed differentiation of bone marrow-derived mesenchymal stem cells. Furthermore, the in vivo experiments suggested that the scaffolds loaded with growth factors promoted osteochondral regeneration in the rabbit knee joint model. Consequently, the biomimetic bilayered scaffold loaded with TGF-β and BMP-2 would be a promising strategy for osteochondral repair.
3D Bio-Printing of CS/Gel/HA/Gr Hybrid Osteochondral Scaffolds

Xueyan Hu,Yuan Man,Wenfang Li,Liying Li,Jie Xu,Roxanne Parungao,Yiwei Wang,Shuangshuang Zheng,Yi Nie,Tianqing Liu,Kedong Song

DOI: https://doi.org/10.3390/polym11101601

IF: 5

2019-09-30

Polymers

Abstract:Cartilage is an important tissue contributing to the structure and function of support and protection in the human body. There are many challenges for tissue cartilage repair. However, 3D bio-printing of osteochondral scaffolds provides a promising solution. This study involved preparing bio-inks with different proportions of chitosan (Cs), Gelatin (Gel), and Hyaluronic acid (HA). The rheological properties of each bio-ink was used to identify the optimal bio-ink for printing. To improve the mechanical properties of the bio-scaffold, Graphene (GR) with a mass ratio of 0.024, 0.06, and 0.1% was doped in the bio-ink. Bio-scaffolds were prepared using 3D printing technology. The mechanical strength, water absorption rate, porosity, and degradation rate of the bio-scaffolds were compared to select the most suitable scaffold to support the proliferation and differentiation of cells. P3 Bone mesenchymal stem cells (BMSCs) were inoculated onto the bio-scaffolds to study the biocompatibility of the scaffolds. The results of SEM showed that the Cs/Gel/HA scaffolds with a GR content of 0, 0.024, 0.06, and 0.1% had a good three-dimensional porous structure and interpenetrating pores, and a porosity of more than 80%. GR was evenly distributed on the scaffold as observed by energy spectrum analyzer and polarizing microscope. With increasing GR content, the mechanical strength of the scaffold was enhanced, and pore walls became thicker and smoother. BMSCs were inoculated on the different scaffolds. The cells distributed and extended well on Cs/Gel/HA/GR scaffolds. Compared to traditional methods in tissue-engineering, this technique displays important advantages in simulating natural cartilage with the ability to finely control the mechanical and chemical properties of the scaffold to support cell distribution and proliferation for tissue repair.

polymer science
HBC-nanofiber hydrogel scaffolds with 3D printed internal microchannels for enhanced cartilage differentiation

Xiaoyun Liu,Shaoshuai Song,Jie Huang,Han Fu,Xinyu Ning,Yong He,Zhijun Zhang

DOI: https://doi.org/10.1039/d0tb00616e

2020-07-22

Abstract:Articular cartilage injuries are a major orthopedic problem. Cartilage repair is a long-standing challenge due to the limited self-regenerative capability of cartilage. Tissue engineering offers a new and effective approach to cartilage repair. We report herein the fabrication of 3D scaffolds that mimic the native structure of cartilage, by first preparing poly(lactic-co-glycolic acid) (PLGA) electrospun nanofiber incorporated hydroxybutyl chitosan (HBC) hydrogels (HBC-NF hydrogels) and then injecting the hydrogels into a 3D printed poly(ε-caprolactone) (PCL) framework with internal microchannels for improved mechanical support and substance exchange. The thus-obtained HBC-NF hydrogels exhibited outstanding gelation properties with a gelling time of no more than 15 s at 37 °C. With the incorporation of the nanofibers, human mesenchymal stem cells (hMSCs) showed good proliferation in the HBC-NF hydrogels. The relative gene expression levels for mesenchymal condensation and matrix deposition significantly increased in the HBC-NF hydrogels due to the addition of the nanofibers, suggesting substantially enhanced cartilage differentiation. Furthermore, the injection of the HBC-NF hydrogels into the 3D printing PCL framework led to the formation of 3D scaffolds with significantly improved mechanical performance. More importantly, the construction of regulable internal microchannels for cell growth and the exchange of nutrients and waste products were achieved via co-printing of PCL and a sacrificial material, Pluronic F-127. The PCL reinforced HBC-NF hydrogel scaffolds with internal microchannels showed enhanced chondrogenesis and mechanical properties in vivo. In summary, the current work has demonstrated that PCL framework reinforced HBC-NF hydrogels with tunable internal microchannels provide an ideal biomimetic microenvironment for the growth and cartilage differentiation of hMSCs, therefore holding promise for potential applications in cartilage tissue engineering.
Direct 3D Printing of High Strength Biohybrid Gradient Hydrogel Scaffolds for Efficient Repair of Osteochondral Defect

Fei Gao,Ziyang Xu,Qingfei Liang,Bo Liu,Haofei Li,Yuanhao Wu,Yinyu Zhang,Zifeng Lin,Mingming Wu,Changshun Ruan,Wenguang Liu

DOI: https://doi.org/10.1002/adfm.201706644

IF: 19

2018-01-17

Advanced Functional Materials

Abstract:Abstract The emerging 3D printing technique allows for tailoring hydrogel‐based soft structure tissue scaffolds for individualized therapy of osteochondral defects. However, the weak mechanical strength and uncontrollable swelling intrinsic to conventional hydrogels restrain their use as bioinks. Here, a high‐strength thermoresponsive supramolecular copolymer hydrogel is synthesized by one‐step copolymerization of dual hydrogen bonding monomers, N ‐acryloyl glycinamide, and N ‐[tris(hydroxymethyl)methyl] acrylamide. The obtained copolymer hydrogels demonstrate excellent mechanical properties—robust tensile strength (up to 0.41 MPa), large stretchability (up to 860%), and high compressive strength (up to 8.4 MPa). The rapid thermoreversible gel ⇔ sol transition behavior makes this copolymer hydrogel suitable for direct 3D printing. Successful preparation of 3D‐printed biohybrid gradient hydrogel scaffolds is demonstrated with controllable 3D architecture, owing to shear thinning property which allows continuous extrusion through a needle and also immediate gelation of fluid upon deposition on the cooled substrate. Furthermore, this biohybrid gradient hydrogel scaffold printed with transforming growth factor beta 1 and β‐tricalciumphosphate on distinct layers facilitates the attachment, spreading, and chondrogenic and osteogenic differentiation of human bone marrow stem cells (hBMSCs) in vitro. The in vivo experiments reveal that the 3D‐printed biohybrid gradient hydrogel scaffolds significantly accelerate simultaneous regeneration of cartilage and subchondral bone in a rat model.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology
Mesenchymal stem cells loaded on 3D-printed gradient poly(ε-caprolactone)/methacrylated alginate composite scaffolds for cartilage tissue engineering

Yanyan Cao,Peng Cheng,Shengbo Sang,Chuan Xiang,Yang An,Xiaochun Wei,Zhizhong Shen,Yixia Zhang,Pengcui Li

DOI: https://doi.org/10.1093/rb/rbab019

2021-04-25

Regenerative Biomaterials

Abstract:Abstract Cartilage has limited self-repair ability due to its avascular, alymphatic and aneural features. The combination of three-dimensional (3D) printing and tissue engineering provides an up-and-coming approach to address this issue. Here, we designed and fabricated a tri-layered (superficial layer (SL), middle layer (ML) and deep layer (DL)) stratified scaffold, inspired by the architecture of collagen fibers in native cartilage tissue. The scaffold was composed of 3D printed depth-dependent gradient poly(ε-caprolactone) (PCL) impregnated with methacrylated alginate (ALMA), and its morphological analysis and mechanical properties were tested. To prove the feasibility of the composite scaffolds for cartilage regeneration, the viability, proliferation, collagen deposition and chondrogenic differentiation of embedded rat bone marrow mesenchymal stem cells (BMSCs) in the scaffolds were assessed by Live/dead assay, CCK-8, DNA content, cell morphology, immunofluorescence and real-time reverse transcription polymerase chain reaction. BMSCs-loaded gradient PCL/ALMA scaffolds showed excellent cell survival, cell proliferation, cell morphology, collagen II deposition and hopeful chondrogenic differentiation compared with three individual-layer scaffolds. Hence, our study demonstrates the potential use of the gradient PCL/ALMA construct for enhanced cartilage tissue engineering.

materials science, biomaterials

What's new in sports medicine.

3D Printing of Biomimetic Multi-Layered GelMA/nHA Scaffold for Osteochondral Defect Repair

3D bioprinting by reinforced bioink based on photocurable interpenetrating networks for cartilage tissue engineering

Daily management systems in medicine.

Fabrication of 3D-Printed Interpenetrating Hydrogel Scaffolds for Promoting Chondrogenic Differentiation

Structurally and Functionally Optimized Silk-Fibroin-Gelatin Scaffold Using 3D Printing to Repair Cartilage Injury In Vitro and In Vivo.

3D Printing of Microenvironment‐Specific Bioinspired and Exosome‐Reinforced Hydrogel Scaffolds for Efficient Cartilage and Subchondral Bone Regeneration

ECM-Mimicking Hydrogels Loaded with Bone Mesenchymal Stem Cell-Derived Exosomes for the Treatment of Cartilage Defects

Experimental study on repair of cartilage defects in the rabbits with GelMA-MSCs scaffold prepared by three-dimensional bioprinting

Bioprinted Biomimetic Hydrogel Matrices Guiding Stem Cell Aggregates for Enhanced Chondrogenesis and Cartilage Regeneration

Cell‐Free Bilayered Porous Scaffolds for Osteochondral Regeneration Fabricated by Continuous 3D‐Printing Using Nascent Physical Hydrogel as Ink

3D printing viscoelastic hydrogel-based scaffolds with a swelling-dependent gate for cartilage injury regeneration

Low temperature 3D printing of tissue cartilage engineered with gelatin methacrylamide.

Low-Temperature Three-Dimensional Printing of Tissue Cartilage Engineered With Gelatin Methacrylamide

A Gelatin-Hyaluronic Acid Double Cross-Linked Hydrogel for Regulating the Growth and Dual Dimensional Cartilage Differentiation of Bone Marrow Mesenchymal Stem Cells.

3D Bioprinting of Bone Marrow Mesenchymal Stem Cell-Laden Silk Fibroin Double Network Scaffolds for Cartilage Tissue Repair

3D Bioprinting of Biomimetic Bilayered Scaffold Consisting of Decellularized Extracellular Matrix and Silk Fibroin for Osteochondral Repair

3D Bio-Printing of CS/Gel/HA/Gr Hybrid Osteochondral Scaffolds

HBC-nanofiber hydrogel scaffolds with 3D printed internal microchannels for enhanced cartilage differentiation

Direct 3D Printing of High Strength Biohybrid Gradient Hydrogel Scaffolds for Efficient Repair of Osteochondral Defect

Mesenchymal stem cells loaded on 3D-printed gradient poly(ε-caprolactone)/methacrylated alginate composite scaffolds for cartilage tissue engineering