Abstract:A red-emitting phosphor Ca 2.91 Si 2 O 7 :0.09Eu 3+ with partial Al 3+ /P 5+ substitution on Si 4+ was synthesized via a simple solid-state method, and the effects of the introduction of the M 3+/5+ (M = Al, P) ions on the crystal structure and photoluminescence performance of Ca 2.91 Si 2− x M x O 7 :0.09Eu 3+ phosphors were investigated. The X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDS), and X-ray photoelectron spectroscopy (XPS) results revealed that the structure of Ca 3 Si 2 O 7 remained the same after the introduction of Al 3+ and P 5+ ions. The characteristic emission of Eu 3+ -doped Ca 3 Si 2− x M x O 7 phosphors exhibited two main peaks at 617 nm (red) and 593 nm (orange) under excitation at 394 nm, which originated from the 5 D 0 → 7 F 2 and 5 D 0 → 7 F 1 electron transitions of Eu 3+ ions. After the partial substitution of Al 3+ and P 5+ , the red emission intensities of the Ca 2.91 Si 2 O 7 :0.09Eu 3+ phosphors were significantly enhanced by 1.88- and 1.42-fold, respectively, which is attributed to the crystal-field effect around Eu 3+ . Meanwhile, the luminescence intensities of the Ca 2.91 Si 1.96 Al 0.04 O 7 :0.09Eu 3+ and Ca 2.91 Si 1.94 P 0.06 O 7 :0.09Eu 3+ phosphors at 210 °C were 79.36% and 77.53% of those at 30 °C, respectively, indicating their excellent thermal stability. Moreover, the as-prepared Ca 2.91 Si 1.96 Al 0.04 O 7 :0.09Eu 3+ and Ca 2.91 Si 1.94 P 0.06 O 7 :0.09Eu 3+ red-emitting phosphors were combined with a near-ultraviolet chip of 395 nm to fabricate red-light-emitting diode (LED) and white (w)-LED devices with excellent chromaticity features. In summary, Al 3+ /P 5+ -substituted Ca 2.91 Si 2 O 7 :0.09Eu 3+ can serve as red-emitting phosphors for applications in w-LEDs.

Photoluminescence enhancement and excellent thermal stability of Ca2ZnSi2O7:Pr3+ red-emitting phosphors through charge compensator A+ (Li+, Na+ and K+) co-doping for w-LED applications

Ca(La1-xEux)4Si3O13 red emitting phosphor for white light emitting diodes

White-light-emitting Diodes Based on Ba2+ Co-Doped Sr3SiO5: Ce3+, Li+ Phosphor

Synthesis and characterization of highly Eu3+-doped CaY2Sb2(ZnO4)3 red phosphors with abnormal thermal quenching performance for w-LEDs application

Simultaneous Enhancement of Red Luminescence and Thermal Stability of a Novel Red Phosphor: A Li+-Eu3+ Co-Occupied Site Strategy in BaAl2Ge2O8 Lattices

Sm3+/Pr3+ biactivated Ca3Y2Ge3O12:0.04Sm3+:Pr3+ red phosphor with high thermal stability for low correlated temperature WLED

Eu3+ Doped Ca3LiSbO6 and Eu3+, Li+ Co-Doped Ca3LiSbO6 Phosphors for White Light-Emitting Diodes

Development of thermally-stable red-emitting lead-free double-perovskite phosphors with an internal PLQY approaching 100%

Multi-Band Emission of Pr3+-Doped Ca3Al2O6 and the Effects of Charge Compensator Ions on Luminescence Properties

Performance improvement of Sr4Al14O25:Mn4+ red emission phosphor via Na+ doping

Preparation and Characterization of Ca1-x-yWO4: Xpr3 + ,yli +deep Red Phosphors for White LEDs Excited by Blue Light

Enhanced Red Emission From Eu3+-Bi3+ Co-Doped Ca2ysbo6 Phosphors For White Light-Emitting Diode

Enhanced red luminescence of Ca3Si2−xMxO7:Eu3+ (M = Al, P) phosphors via partial substitution of Si4+ for applications in white light-emitting diodes

Enhancement of luminescence properties of Ca2Al2SiO7: Eu3+ red phosphors by Li+, Na+, K+, Mg2+ charge compensators

A Highly Thermal Stable and Waterproof Red Phosphor: Pr3+-doped Sr2Al2SiO7

Giant Photoluminescence Improvement and Controllable Emission Adjustment in Bi3+-Activated Ca4ZrGe3O12 Phosphors for High-Quality White Light-Emitting Diodes

Synthesis and Luminescence Properties of a Novel Green-Yellow-Emitting Phosphor BiOCl:Pr 3+ for Blue-Light-Based w-LEDs.

Preparation and Luminescent Properties of a Novel Red Emitting Phosphor of Ca1−2xMxIn2O4:xEu3+ (M = Li, Na, K) for White LED Solid-State Lighting

SrLaNaTeO6:Eu3+ red-emitting phosphors with high luminescence efficiency and high thermal stability for high CRI white LEDs

NaGd0.4Eu0.6Mg1-Zn WO6 solid solution red phosphors: Microstructure variation and luminescence enhancement induced by Zn2+-doping

Tuning Emission Color and Improving the Warm-White Persistent Luminescence of Phosphor BaLu2Al2Ga2SiO12:Pr3+via Zn2+ Co-Doping.