Eco-Friendly Synthesis of Crown-Ether Functionalized Silica Nanospheres from Sorghum Waste for Thallium Adsorption

Saeed Shirazian,Sameer Alshehri,Atiah H. Almalki,Rami M. Alzhrani,Niloofar Pirestani,Roozbeh Soltani
DOI: https://doi.org/10.1016/j.jtice.2024.105851
IF: 5.477
2024-12-08
Journal of the Taiwan Institute of Chemical Engineers
Abstract:Highlights • Eco-friendly synthesis of aza-crown ether silica from sorghum biogenic silica. • Achieved 242 m 2 g –1 surface area with successful aza-crown ether grafting. • Optimal Tl(I) adsorption: 13.1 mg g –1 at pH 9, 25 mL, 60 min, 5 mg adsorbent. • Thallium adsorption is spontaneous, endothermic, and increases surface randomness. • Direct synthesis approach optimizes Tl(I) adsorption for water purification. Background An environmentally sustainable method for synthesizing aza-crown ether functionalized fibrous silica nanospheres was developed using sorghum waste as a biogenic silica source. The goal was to create a novel adsorbent for thallium [Tl(I)] removal from water. Methods A direct synthesis approach was used to anchor aza-crown ether onto the silica fibers. The material was characterized for its fibrous spherical morphology and surface area (242 m 2 g –1 ), and the successful grafting of the functional groups was confirmed. Adsorption studies were conducted to optimize parameters for Tl(I) removal, and kinetic, isothermal, and thermodynamic analyses were performed. Findings The material's maximum adsorption capacity, based on the Langmuir model at 298 K, was 13.1 mg g –1 under optimal conditions (pH 9.0, 25 mL solution, 60 min contact time, 0.2 g L –1 adsorbent, 185 rpm stirring). Kinetic analysis showed a closer fit to the pseudo-first-order model, with three-stage diffusion. Thallium adsorption was endothermic ( ΔHAds.o =38.72 kJ mol –1 ), spontaneous ( ΔGAds.o ranging from –46.81 to –49.68 kJ mol –1 ), accompanied by an increase in surface randomness ( ΔSAds.o =0.287 kJ mol –1 K –1 ). Graphical Abstarct Download: Download high-res image (504KB) Download: Download full-size image
engineering, chemical
What problem does this paper attempt to address?