Abstract:Purpose: This in vitro study aims to evaluate the bonding strengths of Polyether ether ketone (PEEK), Polyether ketone (PEKK), Fiber, and Zirconia (ZrO2) post-core restorations with posts in different diameter and length following chewing simulator. Materials and methods: Endodontic treatment was performed on 256 intact maxillary central teeth. The test specimens were prepared in four groups according to the types of materials: Glass fiber post-composite core (FB-n:64), Zirconia post-core (Zr-n:64), PEEK post-core (PE-n:64), and PEKK post-core (PK-n:64). The groups were divided into four subgroups according to diameter and length (n:16): Group 1: 10 mm length 1.75 mm diameter, Group 2: 10 mm length 1.5 mm diameter, Group 3: 7 mm length 1.75 mm diameter, Group 4: 7 mm length 1.5 mm diameter. Custom PEKK, PEEK, Zirconia post-cores, and Zirconia crowns were milled on the CAD/CAM. The post-cores and crowns were cemented to the teeth with dual-cure resin cement. After that, all subgroups were divided into control and cyclic loading groups. During the cycling, the control test group was kept in distilled water at 37±1oC before the push-out test. Half of the specimens were loaded with 250,000 cycles and 50 N with a chewing simulator. All test specimens had 1.5 mm sections taken from their roots. Then, the push-out test was applied to these sections for bond strength. Data were analyzed by Mann-Whitney U test, Shapiro-Wilk, Kruskal-Wallis's test, and Chi-Square. The statistical significance level was determined as 0.05. Results: The bond strength of all test groups decreased after the cycling loading. The bond strength values of zirconia posts showed a statistically significant difference (p < 0.05). The 10 mm length 1.75 mm diameter posts made of Zirconium had the highest bond strength observed in all control and cyclic loading groups of test specimens (9.74 MPa-6.25 MPa). The PEEK test specimens with a 7 mm length and 1.75 mm diameter showed the weakest bond strength in all control and cyclic loading groups (5.44 MPa-3.37 MPa). The average of the cervical region's bond strength values was statistically significantly higher than the apical region (p < 0.05). Conclusion: Within the limitations of this study, one-piece custom-milled Zirconia post-cores appear promising, as they perform well under functional forces, especially in the anterior region. In addition, custom-milled PEKK post-cores might be considered a suitable alternative to prefabricated fiber-reinforced posts.

Bond strength of various post-core restorations with different lengths and diameters following cycle loading