Enhanced Electrochemical H<sub>2</sub> Evolution by FewLayered Metallic WS<sub>2(1<i>x</i>)</sub>Se<sub>2<i>x</i></sub> Nanoribbons
Fengmei Wang,Jinshan Li,Feng Wang,Zhongzhou Cheng,Zhenxing Wang,Kai Xu,Xueying Zhan,Qisheng Wang,Yun Huang,Chao Jiang,Jun He
2015-01-01
Abstract:© 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim 6077 wileyonlinelibrary.com a promising and sustainable solution to produce H 2 through the transformation of the electrical energy into chemical energy. [ 1 ] A favorable electrocatalyst can promote the conversion from two protons to H 2 (2H + + 2e − → H 2 ) at high reaction rates and low overpotential ( η ). Precious metal platinum (Pt) and its alloys meet the aforementioned requirements and act as excellent electrocatalysts in HER process. [ 2,3 ] However, prohibitive cost and scarcity of Pt hinder the widespread practical application. Presently, the possibility of using earth abundant and inexpensive binary layered transition metal dichalcogenides (TMDs), [ 4 ] such as MoS 2 , [ 5–7 ] WS 2 , [ 8–10 ] MoSe 2 , [ 11–14 ] and WSe 2 , [ 11,12 ] in HER have been investigated. Experimental and theoretical studies indicate that the (10–10) planes on edges of MoS 2 , WS 2 , and WSe 2 are catalytically active for HER due to the low Gibbs free energy for hydrogen absorption (Δ G H o ), while the (0001) basal planes are catalytically inert. [ 6 ] Enormous attempts, thus, have been taken to synthesize lamellar binary layered TMDs exploring lots of edges. [ 13,15,16 ] To further improve the HER activity of these TMDs, many researchers made great effort to optimize Δ G H o through regulating the chemical composition. For example, introducing Co, Fe, and Ni cations [ 17 ] into the TMDbased electrocatalysts has been conducted. The improvement results from the reduced Δ G H o of the edge, which increases the absorbed H coverage and promotes the catalytic activity of active sites. [ 3,17,18 ] Analogously, TMDs with ternary component, such as MoS 2(1− x ) Se 2 x [ 19,20 ] and MoS x Cl y , [ 21 ] are also studied in HER. These composition tunable TMDs demonstrate a better HER performance than their binary counterparts due to the proliferation of unsaturated HER active sites. However, the preparation of composition tunable nanostructures in high yields that are amenable to electrocatalytic application is currently lacking. And compared with the binary ones, the ternary TMDs received relatively little attention, especially for WS 2(1− x ) Se 2 x . In addition to varying their composition, the electroactivity of TMDs can be tuned by altering their electronic structure. Some researches show higher HER activities are realized for the MoS 2 [ 22 ] and WS 2 [ 8,9 ] with 1T phase than that with 2H phase. The appropriate strained metallic 1T phase existed on the surface can positively infl uence Δ G H o , resulting Enhanced Electrochemical H 2 Evolution by Few-Layered Metallic WS 2(1− x ) Se 2 x Nanoribbons