Abstract:The ASTM C1260 and ASTM C1293 are generally accepted as being the best available accelerated tests to evaluate the alkali-silica reactivity of aggregates used in concrete. Unfortunately, these tests have limitations, such as the significant amount of false-positive and false-negative results in ASTM C1260 and the alkali leaching in ASTM C1293, that reduce their accuracy. This paper introduces an alternative test method, the Turner-Fairbank alkali-silica reaction (ASR) susceptibility test (T-FAST) that overcomes traditional limitations of both ASTM standards. In the new test, the ASR was accelerated by exposing the aggregates to a 1 N NaOH solution, three different amounts of CaO, and two temperatures for 21 days. The reactivity index (RI), calculated based on the 21-day concentrations of aluminum, calcium, and silicon in liquid phase, was used to assess the alkali-silica reactivity of 24 well-known aggregates—17 coarse and 7 fine. The results agreed with the classification of the same based on ASTM C1293 and historic field performance available in the literature. The alkali levels at which the ASR reaction was triggered in a selection of aggregates were measured using the T-FAST experimental set up. The threshold alkali values obtained matched those previously reported using accelerated concrete expansion tests as well as with concrete blocks in outdoor exposure sites. The alkali threshold determined for a river sand from Arkansas helped to understand the unexpected ASR distress observed in the field for an aggregate traditionally categorized as nonreactive. This case is a good example of mismatch between the information obtained from accelerated-ASR standard tests and field performance.

Alkali-Silica Reactivity of Aggregate - Concrete Prism Test

Comparison of Field Observations with Laboratory Test Results on Concretes Undergoing Alkali-Silica Reaction

CAN THE ACCELERATED PRISM TEST EVALUATE ALKALI-SILICA REACTIVITY?

Development of an accelerated test on concrete prisms to determine their potential for Alkali-Silica reaction

Characterizing Alkali-Silica Reactivity of Aggregates Using ASTM C 1293, ASTM C 1260, and Their Modifications

Assessment of Alkali–Silica Reactivity of Aggregates by Concrete Expansion Tests in Alkaline Solutions at 38 °C

New Chemical Reactivity Index to Assess Alkali–Silica Reactivity

Reliability of Miniature Concrete Prism Test in Assessing Alkali-Silica Reactivity of Moderately Reactive Aggregates

Evaluating Alkali-Silica Reactivity for Concrete with Recycled Coarse Aggregate Using Concrete Prism and Autoclaved Concrete Prism Test Methods

Divergence between Performance in the Field and Laboratory Test Results for Alkali-Silica Reaction

Alkali-silica reaction (ASR) and alkali-carbonate reaction (ACR) in activated blast furnace slag cement (ABFSC) concrete

ASSESSMENT OF AGGREGATE MIXTURE REACTIVITY IN CONCRETE AT 60°C

Evaluation of Alkali-Silica Reaction Potential of Aggregate Using Dilatometer Method

Monitoring accelerated alkali-silica reaction in concrete prisms with petrography and electrical conductivity measurements

Alkali-silica reaction (ASR) in concrete structures: Mechanisms, effects and evaluation test methods adopted in the United States Case Studies in Construction Materials

ALKALI-AGGREGATE PHASE OF CHEMICAL REACTIVITY IN CONCRETE

Assessment of Alkali–Silica Reaction Potential in Aggregates from Iran and Australia Using Thin-Section Petrography and Expansion Testing

New Turner-Fairbank Alkali-Silica Reaction Susceptibility Test for Aggregate Evaluation

CHEMICAL TESTS FOR ALKALI REACTIVITY OF CONCRETE AGGREGATE

Effect of Grain Size and Reaction Time in Characterisation of Aggregates for Alkali Silica Reaction Using Chemical Method

Alkali-silica reaction products and their development