Tuning multifunctional behavior of PLA/POE‐g‐GMA/MWCNT nanocomposites: Mechanical, rheological, thermal, thermomechanical, and electromagnetic properties
Carlos Bruno Barreto Luna,Fabiano Santana da Silva,Edson Antônio dos Santos Filho,Lorena Vanessa Medeiros Dantas,Debora Pereira Schmitz,Bluma Guenther Soares,Renate Maria Ramos Wellen,Edcleide Maria Araújo
DOI: https://doi.org/10.1002/app.55931
IF: 3
2024-06-27
Journal of Applied Polymer Science
Abstract:PLA/POE‐g‐GMA/MWCNT nanocomposites were processed in the molten state to be used against electromagnetic interference. Obtaining a better distribution of carbon nanotubes promoted greater electromagnetic shielding. Nanocomposites of polylactic acid (PLA) and poly(ethylene‐octene) grafted with glycidyl methacrylate (POE‐g‐GMA) were prepared using multi‐walled carbon nanotubes (MWCNT) as conductive nanofillers. The PLA/POE‐g‐GMA/MWCNT nanocomposites were processed through extrusion and injection molding for rheological, mechanical, electromagnetic, thermal, thermomechanical, and morphological characterization. The carbon nanotubes were dispersed in the PLA/POE‐g‐GMA chain, as seen by Raman spectroscopy. With higher MWCNT content, the complex viscosity (η*) and storage modulus (G') significantly increased in the nanocomposites, suggesting percolation formation. The nanocomposites melt flow index (MFI) results indicated lower fluidity, confirming the trend in η*. Electrical conductivity was optimal for PLA/POE‐g‐GMA/MWCNT (5 phr), reaching a value of 2.21°×°10−6 S/cm and providing electromagnetic shielding of 8 dB across the entire Ku band (12.2–18 GHz). The impact strength of the nanocomposites was higher than that of pure PLA and the PLA/POE‐g‐GMA blend, while the heat deflection temperature (HDT) remained stable at around 56°C. Increased MWCNT content in the nanocomposites promoted recovery of the elastic modulus, tensile strength, and Shore D hardness compared to PLA/POE‐g‐GMA blend. Overall, the results indicate that the PLA/POE‐g‐GMA/MWCNT (5 phr) nanocomposite has potential antistatic applications.
polymer science