Abstract:Fire tests were performed for the first time on adhesively bonded timber‐concrete composite slabs. The two medium‐scale (1.8 × 1.25 m) slabs were produced by gluing an 80‐mm thick three‐layer cross‐laminated timber (CLT) board to a 50 mm thick prefabricated reinforced concrete (RC) slab with epoxy and polyurethane (PUR) adhesives, respectively. The behavior of the composite slabs under elevated temperature was monitored by (1) observing the burning behavior of the used CLT, for example, charring and delamination and (2) measuring the temperature development at different locations of the CLT slabs, in the adhesive bond between concrete and timber boards, and in RC slabs. It was found that employing a one‐dimensional charring model for pure softwood, as prescribed by Eurocode 5‐1‐2, underestimated the charring depth of CLT due to the delamination effects. Measurements revealed that the average charring rates in the middle layer of CLT panels were approximately 0.65 mm/min, suggesting that the presence of concrete does not significantly affect the thermal behavior of the CLT panel. Delamination within the CLT was observed when its adhesive temperature was around 230°C. It was followed by the free‐fall of delaminated wood plies, which progressed slowly and lasted until the end of the test. At 90 min into the test, the temperatures of epoxy at the nine locations ranged between 55°C and 130°, while that of PUR between 60°C and 100°. The adhesive between concrete and CLT could lose stiffness significantly along the rising of temperature after surpassing of glass transition temperature (58°C for epoxy and 23°C for PUR in this study). The results indicated a high risk of weakening the composite action between the concrete slab and timber board. The measured temperatures of steel rebar were lower than 50°C. However, the concrete temperature reached about 120°C and the concrete cracked due to the distinct thermal expansions between concrete and timber and the rigid constraint of adhesive bond.

Experimental study on thermal behaviors of two-layered functionally graded concrete slabs subjected to fire

Evaluation of bond behaviors on functionally graded ultra-high performance concrete (FGUHPC) subjected to elevated temperature

Experimental Study of Flexural Performance of UHPC-NC Laminated Beams Exposed to Fire

Experimental and numerical investigation of fire resistance of G550 galvanized steel-concrete slabs

Bonding Properties Between Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites and Existing Concrete at High Temperatures

Experimental study on shear performance of ultra-high-performance concrete beams at elevated temperatures

Experimental and Numerical Study of the Flexural Performance of Spontaneous Combustion Gangue Coarse Aggregate Concrete Laminated Slab

Experimental study and modelling of flexural behaviour of continuous fibre-reinforced lightweight aggregate concrete one-way slab at ambient and elevated temperatures

Experimental Study on the Structural Performance of Reinforced Truss Concrete Composite Slabs during and after Fire

Research on Fire Resistance of Ultra-High-Performance Concrete

Thermal Resistance, Water Absorption and Microstructure of High-Strength Self-Compacting Lightweight Aggregate Concrete (HSSC-LWAC) after Exposure to Elevated Temperatures

Experimental study and proposal of a design model of ultra-high performance concrete filled steel tube columns subjected to fire

Experimental Investigation and Analysis on Flexural Performance of Functionally Graded Composite Beam Crack-Controlled by Ultrahigh Toughness Cementitious Composites

Study on the fire performance of novel G550 galvanized steel‐concrete composite slabs

Optimizing ultra-high performance cementitious functionally graded composite slab towards bullet impact resistance

Experimental and numerical studies of six small-scale continuous concrete slabs subjected to travelling fires

Resistance and Serviceability Assessment of Innovative Composite Slab Exposed to Standard Compartment Fire

Experimental Research on the Degradation of Mechanical Properties and Microstructural Evolution of Ultra-High-Performance Concrete Under Fire Conditions

Microstructure and mechanical behaviour of 3D printed ultra-high performance concrete after elevated temperatures

Behavior and design of functionally graded concrete subject to triple impacts of the shaped charge, projectile penetration and explosion

Thermal behavior of adhesively bonded timber‐concrete composite slabs subjected to standard fire exposure