Abstract:This study examines the wettability behaviour of 304 stainless steel (304SS) and Ti-6Al-4V (Ti64) surfaces after sequential nanosecond (ns) and picosecond (ps) laser texturing; in particular, how the multi-scale surface structures created influence the lifecycle of surface hydrophobicity. The effect of different post-process treatments is also examined. Surfaces were analysed using Scanning Electron Microscopy (SEM), a white light interferometer optical profiler, and Energy Dispersive X-ray (EDX) spectroscopy. Wettability was assessed through sessile drop contact angle (CA) measurements, conducted at regular intervals over periods of up to 12 months, while EDX scans monitored elemental chemical changes. The results show that sequential (ns + ps) laser processing produced multi-scale surface texture with laser-induced periodic surface structures (LIPSS). Compared to the ns laser case, the (ns + ps) laser processed surfaces transitioned more rapidly to a hydrophobic state and maintained this property for much longer, especially when the single post-process treatment was ultrasonic cleaning. Some interesting features in CA development over these extended timescales are revealed. For 304SS, hydrophobicity was reached in 1-2 days, with the CA then remaining in the range of 120 to 140° for up to 180 days; whereas the ns laser-processed surfaces took longer to reach hydrophobicity and only maintained the condition for up to 30 days. Similar results were found for the case of Ti64. The findings show that such multi-scale structured metal surfaces can offer relatively stable hydrophobic properties, the lifetime of which can be extended significantly through the appropriate selection of laser process parameters and post-process treatment. The addition of LIPSS appears to help extend the longevity of the hydrophobic property. In seeking to identify other factors influencing wettability, from our EDX results, we observed a significant and steady rate of increase in the carbon content at the surface over the study period.

Laser textured superhydrophobic surfaces and their applications for homogeneous spot deposition

Nanosecond Laser Fabrication Of Superhydrophobic Surface On 316l Stainless Steel And Corrosion Protection Application

Superhydrophobic Surfaces with Micro-/Nano-structures Prepared by Femtosecond Laser

Long term superhydrophobic and hybrid superhydrophobic/superhydrophilic surfaces produced by laser surface micro/nano surface structuring

Nanostructuring of laser textured surface to achieve superhydrophobicity on engineering metal surface

Femtosecond laser processed superhydrophobic surface

Superhydrophobic Surface of Ti6Al4V using Direct Nanosecond Laser Texturing

Superhydrophobic microspiked surface structures by ultrashort laser patterning

Wettability Transition for Laser Textured Surfaces: A Comprehensive Review

PFAS-free Superhydrophobic Surfaces using Femtosecond Laser Processing and Hot-Filament Chemical Vapor Deposition

Wettability Behaviour of Metal Surfaces after Sequential Nanosecond and Picosecond Laser Texturing

Scalable Wettability Modification of Aluminum Surface through Single-Shot Nanosecond Laser Processing

Fabrication of Anti-Reflective Surface with Superhydrophobicity/High Oleophobicity and Enhanced Mechanical Durability Via Nanosecond Laser Surface Texturing.

Experimental research on the fabrication and wettability of micro- and nano-scale surface textures produced on stainless steel using an ultrafast laser

Superhydrophobic Surfaces Fabricated by Microstructuring of Stainless Steel Using A Femtosecond Laser

Laser Texturing for Superwetting Titanium Alloy and Investigation of Its Erosion Resistance

Time Dependency of Superhydrophilic and Superhydrophobic Surfaces Produced by Nanosecond Laser Irradiation Assisted by Post-Annealing and Silanization

Construction of superhydrophobic surfaces with different water adhesion on the low-temperature steels by picosecond laser processing

Fabrication of Superhydrophobic Ti–6Al–4V Surfaces with Single-Scale Micotextures by using Two-Step Laser Irradiation and Silanization

Superhydrophobic Surface by Laser Ablation of PDMS

Fabrication of robust superhydrophobic copper surface via highly efficient nanosecond laser-based surface functionalization