Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Low‐cycle fatigue life prediction of powder metallurgy superalloy considering characteristic parameters of inclusions

Prediction of low-cycle crack initiation life of powder superalloy FGH96 with inclusions based on damage mechanics

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

High-temperature Oxidation Behavior of AlCoCrCuFeNi High-Entropy Alloy by Selective Laser Melting

Effect of Inclusion Size and Distribution on Low Cycle Fatigue Properties of an FGH97 Superalloy

Effect of Initial Overload on the Low Cycle Fatigue Life of Gh4169 Alloy at Different Temperatures

An Approach to Estimate the Low Cycle Fatigue Probabilistic Curves of PBF-LB/M 316L Steel from Small Size Datasets Using the Remora Optimization Algorithm

Influence of Non-Metallic Inclusions on Very High-Cycle Fatigue Performance of High-Strength Steels and Interpretation via Crystal Plasticity Finite Element Method

Sem in Situ Observations to the Effects of Inclusions on Initiation and Propagation of the Low Cyclic Fatigue Crack in Super Strength Steel

A novel LCF lifetime model for PM superalloys considering crack energy differences induced by surface underconstraint

Strain‐Controlled Low‐Cycle Fatigue Behavior of a Superalloy Considering Extensive Temperature Range and Stress Concentration

A New Empirical Life Prediction Model For 9-12%Cr Steels Under Low Cycle Fatigue And Creep Fatigue Interaction Loadings

Effect of Surface Modification on the High Temperature Low Cycle Fatigue Performance of LPBF 316L Austenitic Steel

An Approach for Predicting the Low-Cycle-Fatigue Crack Initiation Life of Ultrafine-Grained Aluminum Alloy Considering Inhomogeneous Deformation and Microscale Multiaxial Strain

Predicting multiaxial fatigue life of FGH96 superalloy based on machine learning models by considering failure process and loading paths

Sem In-Situ Investigation on Fatigue Cracking Behavior of P/M Rene95 Alloy with Surface Inclusions

Low Cycle Fatigue Properties of FGH97 P/M Superalloy with Different Test Control Modes

Microstructure evolution, failure mechanism and life prediction of additively manufactured Inconel 625 superalloy with comparable low cycle fatigue performance

The low-cycle fatigue behavior and an entropy-based life prediction model for Nickel-based single crystal superalloy across an extensive temperature range

The Effect of Inclusions on the Fatigue Behavior of Fine-Grained High Strength 42crmovnb Steel

Characteristics of Fatigue Surface Microcrack Growth in Vicinal Inclusion for Powder Metallurgy Alloys