Synthesis of Ti3SiC2 through Pulse Discharge Sintering Powder Mixture Containing Coarse Ti

Yong Zou,Zhengming Sun,H. Hashimoto,Shuji Tada
DOI: https://doi.org/10.2320/MATERTRANS.47.1910
2006-08-20
Abstract:Ternary compound Ti 3 SiC 2 was successfully synthesized by pulse discharge sintering (PDS) for Ti/Si/TiC powder mixtures with different molar ratios, where coarse Ti powder (-0.15 mm) was used. When the molar ratio of Ti:Si:TiC was selected to be 2:2:3, the content of Ti 3 SiC 2 reached 97.8% and density reached 99.0% after sintering at 1450°C for 20 min under 50 MPa load. The Ti-Si liquid reaction occurred above the Ti-Ti 5 Si 3 eutectic temperature at 1330°C is thought to assist the synthesis reaction of Ti 3 SiC 2 as well as densification.