Mitigating Autogenous Shrinkage of Cement with Carbon Nanotube Sponge

Xinming Wang,Jing Zhong

DOI: https://doi.org/10.1016/j.cemconcomp.2024.105571

IF: 9.93

2024-05-03

Cement and Concrete Composites

Abstract:Autogenous shrinkage can be mitigated by the addition of superabsorbent polymer (SAP), however, typically at the cost of a significant strength loss. To overcome such dilemma, hydrophilic carbon nanotube sponge (H-CNTSP) was proposed in this study as a novel internal curing agent. Due to the high porosity and enriched hydrophilic functional groups, H-CNTSP can absorb pore solution at 72 g/g driven by the capillary force, which is 176%-620% higher than the commercial SAPs. The autogenous shrinkage of cement can be reduced or mitigated with the addition of 0.05-0.2 wt. % H-CNTSP due to the continuous water release after final setting. Interestingly, the compressive strength loss resulting from the addition of H-CNTSP can be greatly diminished and even be overcompensated by the formation of CNT/hydrate nanocomposite shell with a higher modulus. This study illustrates the great potential to optimize concrete performance through proper design of assembly structures with chemically functionalized nanomaterials.

construction & building technology,materials science, composites