Rational Design of the Alkali Metal Sn‐Based Mixed Halides with Large Birefringence and Wide Transparent Range
Junbo Wang,Mengmeng Zhu,Yaoqing Chu,Jindan Tian,Lili Liu,Bingbing Zhang,P. Shiv Halasyamani
DOI: https://doi.org/10.1002/smll.202308884
IF: 13.3
2023-12-16
Small
Abstract:Compounds A2Sn2F5Cl (A = Rb and Cs) combine large birefringence (0.28–0.31 at 532 nm), short UV cutoff edge (<300 nm), and wide transparent region (≈0.28–16.6 μm) together, and these merits make them become the alternative birefringent material candidates for optical applications in the UV–vis–IR region. Birefringent materials are widely used in various advanced optical systems, owing to their vital role in creating and controlling polarized light. Currently, Sn2+‐based compounds containing stereochemically active lone‐pair (SCALP) cations are extensively investigated and considered as one class of promising birefringent materials. To solve the problem of relatively narrow bandgap of Sn2+‐based compounds, alkali metals and multiple halogens are introduced to widen the bandgap during the research. Based on this strategy, four new Sn2+‐based halides, A2Sn2F5Cl and ASnFCl2 (A = Rb and Cs), with large birefringence, short ultraviolet (UV) cutoff edge, and wide transparent range are successfully found. The birefringences of A2Sn2F5Cl (A = Rb and Cs) are 0.31 and 0.28 at 532 nm, respectively, which are among the largest in Sn‐based halide family. Remarkably, A2Sn2F5Cl possess relatively shorter UV cutoff edge (<300 nm) and broad infrared (IR) transparent range (up to 16.6 μm), so they can become promising candidates as birefringent materials applied in both UV and IR regions. In addition, a comprehensive analysis on crystal structures and structure–property relationship of metal Sn2+‐based halides is performed to fully understand this family. Therefore, this work provides insights into designing birefringent materials with balanced optical properties.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology