Improving K-Ion Battery Performance By Using K-Metal-Pretreated Electrolyte Solutions
Tomooki Hosaka,Tatsuo Matsuyama,Ryoichi Tatara,Zachary Tyson Gossage,Shinichi Komaba
DOI: https://doi.org/10.1149/ma2023-024555mtgabs
2023-12-22
ECS Meeting Abstracts
Abstract:Nonaqueous K-ion batteries (KIBs) have attracted much attention as a potential high-voltage and high-power secondary battery due to the low standard electrode potential of K + /K in carbonate ester solutions and small Stokes radius of K + ions compared with Li cases. 1 In studies of new electrode materials and electrolytes for KIBs, half-cell measurements using highly reactive K metal counter electrodes are a standard practice. 1 The presence of K metal has been reported to alter both the electrochemical performance and interface chemistry of the working electrode via migration of electrolyte decomposition products across the cell. 2-4 Herein, we systematically evaluated the electrolyte decomposition products formed between K metal and electrolytes prepared with KPF 6 , KN(SO 2 F) 2 (KFSA) or the combined salts (K(PF 6 ) 0.75 (FSA) 0.25 ) dissolved in ethylene carbonate/diethyl carbonate (EC/DEC). 5, 6 To investigate the effect of degradation products on KIB performance, we prepared electrolytes containing KPF 6 , KFSA or K(PF 6 ) 0.75 (FSA) 0.25 dissolved in EC/DEC. We stored 2 mL of each electrolyte in contact with a freshly cut K metal disk with a diameter of 15 mm for 7 days (Figure 1a-d). Then, the K metal was removed, and all the concentration and composition of electrolytes were adjusted to 1 mol kg -1 K(PF 6 ) 0.75 (FSA) 0.25 /EC/DEC by adding either KFSA or KPF 6 , as shown in Figure 1b-d. We denote the obtained electrolytes based on their treatment by K metal (K-KPF 6 , K-KFSA, and K-KPF 6 :KFSA). Using gas chromatography-mass spectrometry (GC-MS) and liquid chromatography-mass spectrometry (LC-MS), we identify significant formation of decomposition products derived from carbonate esters, such as oligocarbonates for K-KPF 6 (Table 1), while K-KFSA predominantly generates anions combining FSA - with the solvent structures (Table 1). Using three-electrode cells, we delineated positive effects of the K-KFSA and K-KPF 6 :KFSA electrolytes on graphite negative electrode performance and the negative impact of oligocarbonates in K-KPF 6 on K 2 Mn[Fe(CN) 6 ] positive electrodes. We further evaluated the K-KPF 6 :KFSA electrolyte in a graphite||K 2 Mn[Fe(CN) 6 ] full cell. As shown in Figure 2a, the initial charge/discharge curves for the K-KPF 6 :KFSA electrolyte (purple) cell exhibited a larger reversible capacity (119 mAh g -1 positive) and higher Coulombic efficiency (CE, 74.5 %) than the untreated electrolyte cell shown in red (110 mAh g -1 and 69.6 %). The improved initial CE for the K-KPF 6 :KFSA electrolyte led to a higher energy density of 277 Wh (kg-active materials) -1 compared with that of 257 Wh kg -1 in the untreated electrolyte. Figure 2b,c displays the CE and capacity retention over 500 cycles. For more than 100 cycles, the K-KPF 6 :KFSA cell continued to demonstrate a higher CE than the untreated electrolyte (Figure 2b), though both cells eventually showed CEs of approximately 99.9%. Furthermore, the use of K-KPF 6 :KFSA improved the full cell’s capacity retention (78%) compared with the untreated cell (72%), as shown in Figure 2c. These results suggest that the electrolyte decomposition products formed by K metal treatment can minimize battery capacity loss by promoting initial SEI formation. Indeed, density functional theory calculation and hard X-ray photoelectron spectroscopy indicated the incorporation of the FSA-derived structures into the solid electrolyte interphase at graphite, which is not observed in K metal-free cells. In the presentation, the impact of electrolyte decomposition products on the electrochemical properties of KIBs’ electrodes and their mechanisms will be further discussed. References: T. Hosaka, K. Kubota, A. S. Hameed and S. Komaba, Chem. Rev. , 2020, 120 , 6358–6466. T. Hosaka, S. Muratsubaki, K. Kubota, H. Onuma and S. Komaba, J Phys Chem Lett , 2019, 10 , 3296-3300. L. Madec, V. Gabaudan, G. Gachot, L. Stievano, L. Monconduit and H. Martinez, ACS Appl. Mater. Interfaces , 2018, 10 , 34116-34122. H. Wang, D. Zhai and F. Kang, Energy Environ. Sci. , 2020, 13 , 4583-4608. T. Hosaka, T. Matsuyama, K. Kubota, S. Yasuno and S. Komaba, ACS Appl. Mater. Interfaces , 2020, 12 , 34873-34881. T. Hosaka and S. Komaba, Bull. Chem. Soc. Jpn. , 2022, 95 , 569-581. Figure 1