Abstract:Atomically dispersed catalysts are a new type of material in the field of catalysis science, yet their large-scale synthesis under mild conditions remains challenging. Here, a general synergistic capture–bonding superassembly strategy to obtain atomically dispersed Pt (Ru, Au, Pd, Ir, and Rh)-based catalysts on micropore-vacancy frameworks at a mild temperature of 60 °C is reported. The precise capture via narrow pores and the stable bonding of vacancies not only simplify the synthesis process of atomically dispersed catalysts but also realize their large-scale preparation at mild temperature. The prepared atomically dispersed Pt-based catalyst possesses a promising electrocatalytic activity for hydrogen evolution, showing an activity (at overpotential of 50 mV) about 21.4 and 20.8 times higher than that of commercial Pt/C catalyst in 1.0 M KOH and 0.5 M H2SO4, respectively. Besides, the extremely long operational stability of more than 100 h provides more potential for its practical application.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.nanolett.2c00042.Materials and methods; SEM, TEM, and EDX images; EDS elemental mapping and line scan results; size distribution, HRTEM, TEM, and EDX mapping images of Pt NPs; Raman spectra; N2 adsorption isotherms curves; comparison of the specific surface areas of MVF obtained at different temperatures; pore distribution curves of different samples; XPS spectra; FT-EXAFS curves of samples at k space; XRD patterns, HR-TEM images, and corresponding SAED patterns of atomically dispersed catalysts; photograph and STEM images of Pt/MVF synthesized on a large scale; electrochemical impedance spectroscopy (EIS) curves; HER polarization curves, variation of Pt content in MVF; polarization curve recorded for Pt/MVF before and after 5000 CV cycles; XRD, XPS spectra, and AC HAADF-STEM image of Pt/MVF before and after stability test; amperometric curve (i–t) measurements; CVs with different rates; testing device for Faradaic efficiency of H2 evolution; inductively coupled plasma results; EXAFS fitting parameters; comparison of catalytic performance for Pt/MVF with other relevant HER electrocatalysts (PDF)Video S1: Measurement of Faraday efficiency by drainage gas collection method (MP4)This article has not yet been cited by other publications.

In situ surface reduction for accessing atomically dispersed platinum on carbon sheets for acidic hydrogen evolution

Highly Active Atomically Dispersed Platinum-Based Electrocatalyst for Hydrogen Evolution Reaction Achieved by Defect Anchoring Strategy

Atomically dispersed platinum supported on curved carbon supports for efficient electrocatalytic hydrogen evolution

Ultrastable monolithic electrodes with single-atom platinum-oxygen sites for efficient hydrogen evolution in acidic conditions

Stable Pt Atomic Clusters on Carbon Nanotubes Grafted with Carbon Quantum Dots As Electrocatalyst for H2 Evolution in Acidic Electrolyte

In-situ anchoring of Pt single atoms on CoFeLDH for efficient alkaline hydrogen evolution reaction

Single-Atom Cr-N4 Sites with High Oxophilicity Interfaced with Pt Atomic Clusters for Practical Alkaline Hydrogen Evolution Catalysis.

Interfacial Proton Transfer for Hydrogen Evolution at the Sub-Nanometric Platinum/Electrolyte Interface

Surface Roughed and Pt-Rich Bimetallic Electrocatalysts for Hydrogen Evolution Reaction

Facilitating alkaline hydrogen evolution reaction on the hetero-interfaced Ru/RuO2 through Pt single atoms doping

Electrochemical Conversion of Bulk Platinum into Platinum Single-Atom Sites for the Hydrogen Evolution Reaction

Surface Confinement Etching and Polarization Matter: A New Approach To Prepare Ultrathin PtAgCo Nanosheets for Hydrogen-Evolution Reactions

Modulating Pt-O-Pt atomic clusters with isolated cobalt atoms for enhanced hydrogen evolution catalysis

General Synergistic Capture-Bonding Superassembly of Atomically Dispersed Catalysts on Micropore-Vacancy Frameworks

Engineering local coordination environment of atomically dispersed platinum catalyst via lattice distortion of support for efficient hydrogen evolution reaction

Hierarchically Stabilized Pt Single-Atom Catalysts Induced by Atomic Substitution Strategy for Efficient Hydrogen Evolution Reaction

Aligned porous carbon film with ultralow loadings of Pt single atoms and clusters for high-current-density hydrogen generation

Single-Atom Cr-N 4 Sites with High Oxophilicity Interfaced with Pt Atomic Clusters for Practical Alkaline Hydrogen Evolution Catalysis

Pt Single-Atom collaborate with Pt Atom-Clusters by an In-Situ confined strategy for accelerating electrocatalytic hydrogen evolution

Anti-dissolution Pt single site with Pt(OH)(O3)/Co(P) coordination for efficient alkaline water splitting electrolyzer

Ultra-low loading Pt atomic cluster electrode with Pt-O bond as an active site with the high hydrogen evolution reaction performance