Phonon-scattering spectra of (Eu2/3Ce1/3)2(Ba2/3Eu1/3)2Cu3O9 and (Er2/3Ce1/3)2(Ba2/3La1/3)2Cu3O9.

Yoshida,Tajima,Mizuo,Wada,Ichinose,Yaegashi,Koshizuka,Yamauchi,Tanaka

DOI: https://doi.org/10.1103/PHYSREVB.44.782

1991-07-01

Abstract:Raman-scattering spectra of (${\mathrm{Eu}}_{2/3}$${\mathrm{Ce}}_{1/3}$${)}_{2}$(${\mathrm{Ba}}_{2/3}$${\mathrm{Eu}}_{1/3}$${)}_{2}$${\mathrm{Cu}}_{3}$${\mathrm{O}}_{9}$ and (${\mathrm{Er}}_{2/3}$${\mathrm{Ce}}_{1/3}$${)}_{2}$(${\mathrm{Ba}}_{2/3}$${\mathrm{La}}_{1/3}$${)}_{2}$${\mathrm{Cu}}_{3}$${\mathrm{O}}_{9}$, both of which have Cu-${\mathrm{O}}_{5}$ pyramid structure, as well as ${\mathrm{YBa}}_{2}$${\mathrm{Cu}}_{3}$${\mathrm{O}}_{7}$, have been observed at room temperature with use of single crystals. A scattering peak with ${\mathit{B}}_{1\mathit{g}}$ symmetry has been observed at around 180 ${\mathrm{cm}}^{\mathrm{\ensuremath{-}}1}$ and peaks with ${\mathit{A}}_{1\mathit{g}}$ symmetry at around 220, 290, 450, and 540 ${\mathrm{cm}}^{\mathrm{\ensuremath{-}}1}$, in both compounds. The 180-${\mathrm{cm}}^{\mathrm{\ensuremath{-}}1}$ peak with ${\mathit{B}}_{1\mathit{g}}$ symmetry is assigned to the out-of-phase bending of oxygen in the Cu-${\mathrm{O}}_{2}$ plane and the 540-${\mathrm{cm}}^{\mathrm{\ensuremath{-}}1}$ peak with ${\mathit{A}}_{1\mathit{g}}$ symmetry to the stretching of apical oxygen. Phonon-energy calculation has been performed with use of ionic potentials obtained for ${\mathrm{YBa}}_{2}$${\mathrm{Cu}}_{3}$${\mathrm{O}}_{7}$. To explain the observed ${\mathit{B}}_{1\mathit{g}}$ phonon energies, it has been found that the polarizability of the oxygen in the Cu-${\mathrm{O}}_{2}$ plane in these compounds must be increased in relation to that in ${\mathrm{YBa}}_{2}$${\mathrm{Cu}}_{3}$${\mathrm{O}}_{7}$. The 220- and 290-${\mathrm{cm}}^{\mathrm{\ensuremath{-}}1}$ peaks are tentatively assigned to the mixed vibrational modes of oxygens in the Cu-${\mathrm{O}}_{2}$ plane and lanthanide atoms.