Abstract:Boehmite (AlOOH) is a stable phases of alumina, which was prepared by addition NaOH solutions to Al(NO3)3.9H2O solution, and further, its surface was modified with (3‐aminopropyl)triethoxysilane. Then, di(pyridin‐2‐yl)methanone was immobilized on the surface of modified AlOOH as a heterogeneous Schiff‐base ligand. In the final step, a palladium complex was stabilized on its surface (Pd‐di(PM)@AlOOH) as a reusable, practical, and novel catalyst in the C‐C coupling of Suzuki reaction. This catalyst was characterized by TGA, FT‐IR, TEM, SEM, EDS, WDX, and ICP techniques. Due to recoverability and heterogeneous nature of this catalyst, it can be reused for several runs without palladium leaching or any reactivation. Boehmite is one of the stable phases of alumina that is easily available, and it also has a variety of applications. Therefore in this work, for preparation of AlOOH, Sodium hydroxide (NaOH) solutions was added to aluminum nitrate nonahydrate (Al(NO3)3.9H2O) solution. Then, the surface of AlOOH was modified with (3‐aminopropyl)triethoxysilane (APTES), due to high condensation of hydroxyl groups on its surface. Then, di(pyridin‐2‐yl)methanone (di(PM)) was immobilized on the surface of modified AlOOH toward synthesis of immobilized Schiff‐base on AlOOH (di(PM)@AlOOH) as a heterogeneous Schiff‐base ligand. Finally, a palladium complex was immobilized on its surface (Pd‐di(PM)@AlOOH) as a reusable, practical, and novel nanocatalyst. Pd‐di(PM)@AlOOH was characterized by thermogravimetric analysis (TGA) analysis, Fourier‐transform infrared spectroscopy (FT‐IR), transmission electron microscopy (TEM), scanning electron microscope (SEM) imaging, energy‐dispersive X‐ray spectroscopy (EDS) analysis, wavelength‐dispersive X‐ray spectroscopy (WDX) analysis, and inductively coupled plasma (ICP) analysis. After the characterization of Pd‐di(PM)@AlOOH, its performance was used as a highly practical, stable, retrievable, and hybrid organic–inorganic catalyst in the C‐C coupling of the Suzuki reaction. The hot filtration study of Pd‐di(PM)@AlOOH revealed that it acts heterogeneously in the Suzuki reaction. We found that this catalyst can be recycled for five runs without palladium leaching, as studied by hot filtration test and ICP analysis.

Immobilizing of palladium on melamine functionalized magnetic chitosan beads: A versatile catalyst for p-nitrophenol reduction and Suzuki reaction in aqueous medium

A Conveniently Synthesized Polyethylene Gel Encapsulating Palladium Nanoparticles As A Reusable High-Performance Catalyst For Heck And Suzuki Coupling Reactions

New chelating N‐heterocyclic carbene palladium complexes immobilized on magnetic nanoparticles: Synthesis, characterization, and catalytic properties

Chitosan-functionalized poly(3-hydroxybutyrate) bead as a novel biosupport for palladium in the Suzuki cross-coupling reaction

Functionalized chitosan as a novel support for stabilizing palladium in Suzuki reactions

Palladium nanoparticles on polydimethylsiloxane film for C−C coupling reactions, and catalytic reduction of organic pollutants in water

Palladium Immobilized on a Polyimide Covalent Organic Framework: An Efficient and Recyclable Heterogeneous Catalyst for the Suzuki–Miyaura Coupling Reaction and Nitroarene Reduction in Water

Novel Water Dispersible and Magnetically Recoverable Palladium Nano Catalyst for Room‐Temperature Suzuki‐Miyaura Coupling Reaction

Immobilization of palladium on benzimidazole functionalized mesoporous silica nanoparticles: catalytic efficacy in Suzuki–Miyaura reaction and nitroarenes reduction

In situ green immobilization of palladium nanoparticles onto polydopamine-modified eggshell membrane for catalytic reduction of nitrophenols

Palladium-Decorated Covalent Organic Framework Supported on Zinc Ferrite as Magnetic Catalyst for Suzuki Reaction and p-nitrophenol Reduction

Palladium Nanoparticles Anchored on Magnetic Organic–Inorganic Hybrid 3D-Network Polymer: A Nanocatalyst for Reduction of Nitro Compounds and Suzuki–Miyaura Coupling

Hierarchical Fe3O4 microspheres supported chitosan/palladium nanocomposite as a recyclable catalyst

A new Schiff‐base complex of palladium nanoparticles on modified boehmite with di(pyridin‐2‐yl)methanone as a robust, reusable, and selective nanocatalyst in the C‐C coupling reaction

Palladium nanoparticles supported on fluorine-doped tin oxide as an efficient heterogeneous catalyst for Suzuki coupling and 4-nitrophenol reduction

Mesoporous silica nanospheres supported atomically precise palladium nanocluster: Highly efficient and recyclable catalysts in the reduction of 4‐nitrophenol and Heck reactions

A highly controllable, effective, and recyclable magnetic-nanoparticle-supported palladium catalyst for the Suzuki-Miyaura cross-coupling reaction

Palladium nanoparticles anchored on NiO particles-modified micro-size chitosan spheres: A promising, active, and retrievable catalyst system for treatment of environmental pollutants

Palladium nanoparticles embedded polyimide derived carbon nanofibers for Suzuki reactions

Iron Oxide Nanoparticles Modified with Carbon Quantum Nanodots for the Stabilization of Palladium Nanoparticles: An Efficient Catalyst for the Suzuki Reaction in Aqueous Media under Mild Conditions

Preparation of PdNi bimetallic loaded amino modified porous carbon material catalyst based on chitosan and its applications